Resistance Steps And Asymmetric Conduction Induced By Currents In La0.8ca0.2mno3 Films

Jianfeng Wang,Ju Gao,Lin Wang

DOI: https://doi.org/10.1109/TMAG.2010.2044752

IF: 1.848

2010-01-01

IEEE Transactions on Magnetics

Abstract:A constant voltage mode of a power supply was adopted to study the current-induced effects in La0.8Ca0.2MnO3 epitaxial thin films. After processed by a current of the density of similar to 3 x 10(5) A/cm(2) for 1 minute, they exhibited anisotropic conduction. Like the behavior of p-n junctions, the current starts to increase dramatically in the forward direction at a threshold voltage (opening voltage V-OP), e.g., similar to 2.3 V at 30 K. For a processing with extending duration, the resistance while processing dropped from 10 k Omega to 2 k Omega. Current voltage curves measured following such a step showed more stable asymmetric characteristics and substantial reduction of V-OP, which is similar to 0.8 V at 290 K and similar to 1.6 V at 50 K. Our results are useful for revealing the origin of asymmetric conduction induced by current and for potential application.