Defect center–tailored calcium aluminate glasses for photonic applications: Unveiling structure–diffusivity correlation
Saswata Chakraborty,Indrajit Tah,Anustup Chakraborty,Sushanta K. Mohapatra,Himanshu S. Maharana,Kancharla Hari Krishna,Krishna K. Dey,Prince Sen,Sathravada Balaji,Kaushik Biswas,K. Annapurna
DOI: https://doi.org/10.1111/jace.20274
IF: 4.186
2024-12-01
Journal of the American Ceramic Society
Abstract:The composition modification by the inclusion of Li2O, Na2O, K2O, and GeO2 in barium–zinc–CA glasses can limit the excess oxygen defect formation with their charge compensator or glass former role. Highly diffusive Li and Na‐glasses reduce the O3− centers, whereas those are promoted in K‐glasses compared to base glass. However, GeO2 addition reduces all the defects significantly. This is further confirmed by optical probing with Cr ions that displays broadband near‐infrared emission in selected glasses. Calcium aluminate (CA)‐based glasses have drawn significant attention owing to their pronounced optical, mechanical, and chemical properties for potential applications in IR photonics. Nonetheless, limitations related to their poor glass‐forming ability was addressed by incorporating ZnO that has formed negatively charged [ZnO4]2− and [AlO4]− units, thereby generating the oxygen‐excess defects. These defects impart a detrimental effect on the optical properties. Thus, the present study explores the impact of Li2O, Na2O, K2O, and GeO2 inclusion in the barium–zinc–calcium–aluminate (BZCA) glass to eliminate the oxygen‐excess defects. The molecular structure of the glass matrix was examined by Raman, NMR, and XPS along with the bulk diffusivity of the glasses through MD simulation and are correlated to elucidate the origin of the defect centers. Due to higher diffusivity, Li+ and Na+ cations decrease Al–O hole centers (Al–OHC) and O3− defects but promote F+ (Farbe) centers while K+ ions having lower diffusivity and enhance the O3− defects. Interestingly, all the defect centers are substantially reduced in GeO2‐containing glasses. Further, multivalent Cr ions are doped to optically probe the defect centers through UV–Vis–NIR absorption and photoluminescence spectra. Cr3+ and Cr4+ are found dominant in Li+‐and Na+‐containing glasses due to the presence of less O3− defect, whereas excess O3− converts all Cr3+ into Cr6+ for K+‐containing glasses. Additionally, broadband NIR emission from Cr4+ can functionalize selective glasses for laser and telecommunication applications.
materials science, ceramics