Abstract:Electrochemical deposition (ED) has been proposed as a low temperature approach for preparing hydroxyapatite (HA) coatings. To overcome the problem of low adhesion, the preparation of thin and low-porosity coatings on Ti substrates pre-treated by micro-arc oxidation (MAO) is a good strategy. In this paper, a thin and dense HA coating was obtained by modifying parameters at pH 6.4, 45 °C, and 0.5 mA·cm −2 . The growth behaviours of HA electrodeposited on MAO coatings were investigated by SEM and EDS technology and summarized that the HA was initially generated in the MAO micropores, then covered the entire MAO surface and gradually grew outwards. This growth pattern was also confirmed by ATR-FTIR, XPS, EIS, open potential, and wettability results at different ED cycles. Adjusting 1:1 power-on/off time ratio affected the morphology of HA grown in the pores in the early stage and also increased the interfacial strength, up to 10.69 MPa at duty cycle 12/24.The cross-section of the final specimen was characterised by TEM and EDS, indicating that amorphous layers, nanocrystalline HA, and submicron HA were formed sequentially from the TiO 2 (Ca)/HA interface outwards. The increase in Ca 2+ concentration and the formation of CaO bonds at the interface may be important reasons for the adhesive enhancement. This process provides a strategy to enhance the strength of bioceramic materials on Ti substrates.

Kinetic Model for Hydroxyapatite Precipitation on Human Enamel Surface by Electrolytic Deposition

Electrolytic Deposition of Hydroxyapatite Coating on CoNiCrMo Substrates

Effect of EDTA on Electrodeposition of Hydroxyapatite Coatings

Synthesis and Characterization of Zn-substituted Hydroxyapatite Coatings by Electrochemical Deposition

Effect of Supersaturation on the Morphology of Hydroxyapatite Crystals Deposited by Electrochemical Deposition on Titanium

Morphologies of Hydroxyapatite Crystal Deposited on Titanium Surface with Electrochemical Technique

Electrodeposition of Hydroxyapatite Coating on CoNiCrMo Substrate in Dilute Solution

Synthesis and Charaterization of Silicon-Substituted Hydroxyapatite Coating by Electrochemical Deposition on Ti Substrate

Effect of Trisodium Citrate on Electrolytic Deposition of Hydroxyapatite Coatings

Ribbon-like and rod-like hydroxyapatite crystals deposited on titanium surface with electrochemical method

Electrolytic Deposition of Magnesium-Substituted Hydroxyapatite Crystals on Titanium Substrate

Preparation of hydroxyapatite coating on smooth implant surface by electrodeposition

A Study of the Process and Kinetics of Electrochemical Deposition and the Hydrothermal Synthesis of Hydroxyapatite Coatings

Evolution of the magnesium incorporated amorphous calcium phosphate to nano-crystallized hydroxyapatite in alkaline solution

Electrochemical Deposition Technology Regulating the Morphology of Hydroxyapatite Deposited on Silk Fibroin Film

Recent advances in multifunctional hydroxyapatite coating by electrochemical deposition

Preparation and growth behaviours of low porosity hydroxyapatite with enhanced adhesion by electrochemical deposition on micro-arc oxide coatings

Hydroxyapatite Film Coating by Er:YAG Pulsed Laser Deposition Method for the Repair of Enamel Defects

Study of Process and Properties of the Hydroxyapatite Biocoatings Fabricated by Electrocrystallization and Hydrothermal Synthesis

Simultaneous Precipitation and Electrodeposition of Hydroxyapatite Coatings at Different Temperatures on Various Metal Substrates

Electrohydrodynamic Coating of Metal with Nano-Sized Hydroxyapatite.