Abstract:In this study, the addition of the rare earth oxide CeO2 was investigated to alter the microstructural properties of the nano-WC-reinforced Ni-based composite coatings. The reinforced composite was prepared on the 42CrMo steel surface using a semiconductor laser. The morphology and microstructure of coatings were analyzed using a scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD). Further, the digital microhardness tester and high-temperature friction and wear tester were used to observe the mechanical properties. The results indicated that the addition of CeO2 eliminated the cracks from the surface of the coatings and effectively reduced the number of pores. The phases were mainly observed as γ-Ni(Fe) in a solid solution, and some residual WC and W2C phases were observed. In addition, Fe3C, Cr23C6, M6C (M = W, Fe, and Ni), SiC and Cr7C3 composite carbides, Si2W and NiW tungsten compounds, and CeFe2- and CeNi2-containing Ce complex compounds were formed on the coating. The rare earth oxide CeO2 composite-modified coating mainly comprised dendrites, crystal cells, strips, and massive microstructures. The reinforced phases of the modified coating presented uniform dispersion distribution with the addition of 1% CeO2, and the structures were significantly refined. The maximum microhardness of the modified coating was approximately 1560 HV0.2, which was approximately 20% higher than that of the unmodified composite coating. The minimum wear loss of the modified coating was 6.1 mg and the minimum frictional coefficient was approximately 0.23, which were better than those of the unmodified coating. The wear mechanism of the nano-WC-reinforced Ni-based coating was primarily adhesive, whereas that of the CeO2 composite modified coating was mainly abrasive particle wear, which accompanied adhesive wear.

Rare earth effect on microstructure, mechanical and tribological properties of CoCrW coatings

Rare earth effect on the microstructure and wear resistance of Ni-based coatings

Tribological properties of rare earth oxide added Cr3C2–NiCr coatings

Tribological Properties of La2O3 and CeO2 Doped CoCrW Coatings Deposited by Supersonic Plasma Spraying

Effect of Rare Earth on WC-12Co Coatings Prepared by Thermal Spraying

Study on Wear Performance of Rare-earth Modified WC/12Co Thermally Sprayed Coatings

Rare Earth's Influence on Wear Resistance of Spray-melted Coatings with Mixture of Ni60B and 35Mass.%wc

Effects Of Wc Crystal Characteristics On Microstructure And Mechanical Property Of Hvof-Sprayed Wc-Cocr Coatings

Effects of WC mass fraction on microstructure and tribological behavior of plasma sprayed FeMnCoCr–WC coatings

Effect of the Rare Earth Oxide CeO2 on the Microstructure and Properties of the Nano-WC-Reinforced Ni-Based Composite Coating

Effect of Rare Earth on the Microstructure and Performance of Electrodeposited Ni-W Coatings

Microstructure, Mechanical and Tribological Properties of WC-WCoB Coating

Effect of nano-La2O3 doping on the tribological behavior of laser cladded WC-12Co coating on 65Mn steel under water lubrication condition

Effect of Cobalt and Chromium Content on Microstructure and Properties of WC-Co-Cr Coatings Prepared by High-Velocity Oxy-Fuel Spraying

Rare earth-doped ceramic coatings: Analysis of microstructure, mechanical properties, and slurry Erosion resistance using high pressure-high velocity oxy-liquid fuel deposition

Structure and water-lubricated tribological properties of Cr/a-C coatings with different Cr contents

Comparative tribological study of air plasma sprayed WC–12%Co coating versus conventional hard chromium electrodeposit

Rare Earth Surface Engineering—Improving the Tribological Properties of Materials

Influence of Solid Chromizing Doped with Various Rare Earths on Microstructures and Properties of Cr-RE Coatings Fabricated by Pack Cementation

Microstructure and mechanical property of high velocity oxy-fuel sprayed WC-Cr3C2-Ni coatings

Microstructure, mechanical properties and wear resistance of rare earth doped WC/steel matrix composites:Experimental and calculations