Microstructure, interface characteristics and tribological properties of laser cladded NiCrBSi-WC coatings on PH 13-8 Mo steel

Xingchen Yan,Cheng Chang,Zhaoyang Deng,Bingwen Lu,Qingkun Chu,Xingchi Chen,Wenyou Ma,Hanlin Liao,Min Liu
DOI: https://doi.org/10.1016/j.triboint.2021.106873
IF: 5.62
2021-05-01
Tribology International
Abstract:<p>Multiple NiCrBSi-WC coatings with good macro morphology and uniform microstructure were manufactured on PH 13-8Mo steel substrate using laser cladding (LC) technology. Microstructure, interface characteristics and tribological properties of the laser cladded NiCrBSi-WC coatings were researched utilizing optical microscope (OM), X-ray diffraction (XRD), and scanning electron microscopy (SEM) equipped with an energy-dispersive X-ray spectroscopy (EDS) unit. In XRD pattern of the NiCrBSi-WC coatings, γ-(Ni, Fe) solid solutions with numerous secondary carbides and intermetallic compounds can be found including W<sub>2</sub>C, Ni<sub>3</sub>B, and M<sub>23</sub>C<sub>6</sub>. Cooling rate of this LC process can be determined as 1.5×10<sup>6</sup> K/s. Ultra-high hardness secondary carbides evenly distributed in the fine γ-(Ni, Fe) columnar dendrites can be observed in the coatings. From top of the coatings to the substrate, the averaged microhardness of the coatings, dilution area, heat-affected zone and substrate is 1008±48.2 HV<sub>0.2</sub>, 842±31.8 HV<sub>0.2</sub>, 386±24.4 HV<sub>0.2</sub>, 356±3.0 HV<sub>0.2</sub>, respectively. The coatings presented the best tribological properties with the lowest average coefficient of friction (COF=0.28) and the wear rate (3.92±0.72×10<sup>-6</sup> mm<sup>3</sup>/(N•m)). A step feature can be observed in the dynamic stable wear process of the interface at the coating/substrate. Good tribological performances of the interface at the coating/substrate with low average COF (0.40) and wear rate (31.83±2.12×10<sup>-6</sup> mm<sup>3</sup>/(N•m)) can be obtained.</p>
engineering, mechanical
What problem does this paper attempt to address?