Abstract:We propose a facile and continuous direct nitridation method for synthesizing fine aluminum nitride (AlN) particles using a drop tube furnace. Aerosolized Al powder as the raw material was continuously supplied through the top of the furnace together with N2 as a carrier gas. Once in the furnace, the Al powder reacted with the N2 to form AlN. A particular advantage of this process is that it allows the continuous synthesis of fine AlN particles. In this study, either a mullite (Al2O3–SiO2) or an alumina tube was used to fabricate the furnace, and the products were collected in a crucible placed at the bottom. Upon heating the mullite tube from 1200 to 1400°C, AlN was formed once the temperature exceeded 1250°C, and its product content increased with temperature. When the flow rate of the N2 carrier gas was decreased from 4 to 2 L min−1, the amount of AlN formed increased due to the increased residence time in the reactor. The morphology of the particles obtained was radially aligned nanofibers with droplets on the tips of the fibers. Transmission electron microscopy revealed that the Si in the mullite tube reacted with Al to form eutectic Al–Si droplets on the Al surface, in which these droplets acted as a catalyst of vapor–liquid–solid AlN fiber growth. When the alumina tube was used (1800°C), nitridation of Al was enhanced and radially aligned AlN nanofibers with no droplets on the tips were collected, mainly in a filter at the exhaust port. These AlN nanofibers are thought to form via vapor–solid growth and are easily carried along with the N2 gas flow, resulting in their deposition on the filter. The products collected in the crucible contained coarse Al particles, which are formed via Al particle agglomeration and coarsening through melting.

Preparation of ultrafine composite particles of Ag+AlN/Al by nitrogen plasma metal reaction

Preparation of Metal Nitride Particles Using Arc Discharge in Liquid Nitrogen

Preparation of Ag-Al2O3 nano-composites powder

Facile synthesis of monodisperse aluminum nitride microspheres

Fabrication of Carbon-Coated Aluminum Nanoparticles and Carbon Quantum Dots by Thermal Plasma in Liquid Nitrogen Environment

Synthesis of nearly spherical AlN particles by an in-situ nitriding combustion route

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

In Situ Synthesis of Carbon-Coated Aluminum Nanoparticles by Argon Protective Arc Ablation in the Liquid Nitrogen Environment

Preparation of ti-al based nanophase composite powder by mechanical alloying

Highly Crystalline Aln Particles Synthesized by Shs Method

Preparation of NiAl2O4/Al2O3 composite nanopowder

In-situ formation of AlN/Al composite

Synthesis of AlN particles via direct nitridation in a drop tube furnace

Toward homogenous AlN via reaction of Al nanoparticles with N 2 and NH 3 : Reactive molecular dynamics simulation

Synthesis of Ultrafine AlN Powders in an Al-OC-N System

Synthesis of Aluminum Nitride Powders from A Plasma-Assisted Ball Milled Precursor Through Carbothermal Reaction

Enhancing the combustion of nAl with AlF 3 coating: gas–solid reaction mechanism for reducing combustion agglomeration of Al powder

Combustion Synthesis of Rod-Like AlN Nanoparticles

In Situ Synthesis of AlN Nanoparticles by Solid State Reaction from Plasma Assisted Ball Milling Al and Diaminomaleonitrile Mixture

Novel Way to Synthesize Nanocrystalline Aluminum Nitride from Coarse Aluminum Powder

Synthesis and structural features of Ni–Al nanoparticles by hydrogen plasma–metal reaction