Abstract:The terpolymer latex of methyl methacrylate (MMA)/butyl acrylate (BA)/dimethylaminoethyl methacrylate (DMAEMA) was prepared by batch and semi-continuous emulsion copolymerization. The effects of emulsifier type and concentration, polymerization temperature, and feed policy of emulsified monomers on process stability of the copolymerization and properties of the terpolymer latex were studied systematically. The results suggest that the selection of emulsifier should not be based on the HLB values for the DMAEMA-containing systems. The co-emulsifiers suitable for stabilizing the copolymerization process are in the order of SDS/OP>SDBS/OP>OT/OP. The results also indicate that an increase in amount of the co-emulsifiers, sodium dodecyl sulfate (SDS) and octyl phenol polyoxyethyl ether (OP), improves the process stability, decreases the surface tension and particle size of latices; however, it has little influence on the electrolyte stability when SDS/OP ratio is unchanged. A decrease in reaction temperature improves the process stability of polymerization but decreases the electrolyte stability of latices. The DMAEMA content does not affect the process stability significantly under investigated conditions but contributes to improve the electrolyte stability of latices. Compared to the batch polymerization process, the semi-continuous polymerization with a lower monomer feed rate provides better process stability for the polymerization and better electrolyte stability for the latices.

The Effects of Post‐Addition Rate on Polymerization Rate and Molecular Weight in Modified Microemulsion Polymerization of MMA

Emulsion polymerization of methyl methacrylate in concentration of emulsifiers below their CMCs—polymerization rate, particle size, and particle-size distribution

Preparation and Characterization of MMA-BA-DMAEMA Terpolymer Latex

Stability of Emulsion Copolymerization of Acrylic Monomers Containing Amino and Hydroxyl Groups

Stability of the emulsion copolymerization process of the latex containing glycidyl and amino groups

Online Monitoring Of Drop/Particle Size And Size Distribution In Liquid-Liquid Dispersions And Suspension Polymerizations By Optical Reflectance Measurements

Reversible addition–fragmentation chain transfer polymerization of methyl methacrylate in emulsion

Kinetics of Suspended Emulsion Polymerization of Methyl Methacrylate

RAFT miniemulsion polymerization of methyl methacrylate

Study of Kinetic of Emulsion Copolymerization of Methyl Methacrylate/ethyl Acrylate

Synthesis of Nanosize Poly(methyl Methacrylate) Microlatexes with High Polymer Content by a Modified Microemulsion Polymerization

Electrostatic Absorption of Initiator Onto Nanometer SiO2 Particles and In-Situ Emulsion Polymerization of Methyl Methacrylate in the Presence of Modified Nanometer SiO2

The effect of monomer polarity on MMA/BA/ Sodium methacrylate emulsifier-free emulsion copolymerization

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Effects of Monomer Polarity on Mma/Ba/Nama Emulsifier-Free Emulsion Copolymerization

Kinetic and Molecular Weight Control for Methyl Methacrylate Semibatch Polymerization. II. Open Control

Emulsion copolymerization of MMA/BA in the presence of surface active monomers (II) - Kinetics and polymerization mechanism

Kinetics of Styrene-Methyl Methacrylate Suspension-Emulsion Combined Polymerization

Particle Features of A Poly(Methyl Methacrylate) Resin Prepared by A New Emulsion Polymerization Process

In-Situ Heterogenous Polymerization of Methyl Methacrylateonto Nanometer Calcium Carbonate Particles

Study on nano-size PMMA particles prepared by O/W microemulsion polymerization. - (1) Phase diagram, compatibilization and reaction kinetics