Preparation and Characterization of MMA-BA-DMAEMA Terpolymer Latex

ZQ Yu,BG Li,BF Li,ZR Pan

DOI: https://doi.org/10.1016/s0927-7757(98)00423-3

1999-01-01

Abstract:The terpolymer latex of methyl methacrylate (MMA)/butyl acrylate (BA)/dimethylaminoethyl methacrylate (DMAEMA) was prepared by batch and semi-continuous emulsion copolymerization. The effects of emulsifier type and concentration, polymerization temperature, and feed policy of emulsified monomers on process stability of the copolymerization and properties of the terpolymer latex were studied systematically. The results suggest that the selection of emulsifier should not be based on the HLB values for the DMAEMA-containing systems. The co-emulsifiers suitable for stabilizing the copolymerization process are in the order of SDS/OP>SDBS/OP>OT/OP. The results also indicate that an increase in amount of the co-emulsifiers, sodium dodecyl sulfate (SDS) and octyl phenol polyoxyethyl ether (OP), improves the process stability, decreases the surface tension and particle size of latices; however, it has little influence on the electrolyte stability when SDS/OP ratio is unchanged. A decrease in reaction temperature improves the process stability of polymerization but decreases the electrolyte stability of latices. The DMAEMA content does not affect the process stability significantly under investigated conditions but contributes to improve the electrolyte stability of latices. Compared to the batch polymerization process, the semi-continuous polymerization with a lower monomer feed rate provides better process stability for the polymerization and better electrolyte stability for the latices.