Abstract:Purpose – The purpose of this research was to synthesize a novel cross-linked latex copolymerised by butyl acrylate (BA), isobornyl methacrylate (IBOMA), hydroxy propyl methacrylate (HPMA) and dodecafluoroheptyl methacrylate (DFMA). IBOMA is a very useful functional monomer. Its molecular structure not only contains bornyl acetate alkoxy but also includes a double bond, which can be copolymerised with other unsaturated monomers via free radical polymerization. The large nonpolar bicyclic alkyl in bornyl acetate alkoxy offers the polymer chain strong space steric protection, which endows the polymer with some special properties. Design/methodology/approach – The semi-continuous seeded emulsion polymerisation technology was adopted to copolymerise BA, IBOMA, HPMA and DFMA in the water phase, which was initiated with potassium persulfate (KPS) and emulsified with the mixed surfactants of sodium dodecyl sulphate (SDS) and OP-10. Findings – The particle size of the latex decreases with an increase in the amount of IBOMA. All the latexes have good mechanical stability and calcium ion stability. The latex has good film-forming property when the IBOMA amount is controlled moderately. The optimal IBOMA amount is 10.00 g. The thermal stability and water resistance of the film are improved. Practical implications – The latexes can be applied as a binder of coatings and adhesions. Originality/value – The effect of the amount of IBOMA and BA on the properties of the resultant latex and its film were investigated in detail. In comparison with the latexes copolymerised without IBOMA, the novel latex has better thermal stability and water resistance.

Emulsion copolymerization of MMA/BA in the presence of surface active monomers (III) - Latex stability

Stability of Emulsion Copolymerization of Acrylic Monomers Containing Amino and Hydroxyl Groups

Preparation and Characterization of MMA-BA-DMAEMA Terpolymer Latex

Stability of the emulsion copolymerization process of the latex containing glycidyl and amino groups

Emulsion Polymerization of Mma/Ba in the Presence of Ionic Surface Active Monomers (I) - Syntheses and Polymerization Reactivities of the Surfmers

Stability Of The Ghd Latex Crosslinkable At Ambient Temperature

Stability Of Emulsifier-Free Emulsion Copolymerization Of Methyl Methacrylate/Butyl Acrylate/Sodium Mono(Ethyl Polyoxyethylene)Maleate

Stability of Emulsifier-free Emulsion Copolymerization of MMA/BA/Comonomer with Two Functional Groups

Seed Semicontinuous Emulsion Multi-Copolymerization of (meth)acrylates with High-Solid Content - Effect of the Operation Conditions

Switchable Block Copolymer Surfactants for Preparation of Reversibly Coagulatable and Redispersible Poly(Methyl Methacrylate) Latexes

Emulsion copolymerization of MMA/BA in the presence of surface active monomers (II) - Kinetics and polymerization mechanism

The effect of monomer polarity on MMA/BA/ Sodium methacrylate emulsifier-free emulsion copolymerization

The Influence of Monomer Types on the Colloidal Stability in the Miniemulsion Copolymerization Involving Alkoxysilane Monomer

Effects of Monomer Polarity on Mma/Ba/Nama Emulsifier-Free Emulsion Copolymerization

Preparation and Characterisation of Novel Cross-Linked Poly (IBOMA-BA-DFMA) Latex

Preparation of Mma-Ba-Dmaema Nanosized Latex

Formation of Monodispersed Polymer Particles in Emulsifier-Free Emulsion Polymerization

Synthesis and Properties of the FA/LMA/MMA Copolymer Emulsion

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

Synthesis and Characterization of Self-cross Linking Hybrid Silicone-acrylate Emulsion at Ambient Temperature

Electrostatic Absorption of Initiator Onto Nanometer SiO2 Particles and In-Situ Emulsion Polymerization of Methyl Methacrylate in the Presence of Modified Nanometer SiO2