Abstract:The terpolymer latex of methyl methacrylate (MMA)/butyl acrylate (BA)/dimethylaminoethyl methacrylate (DMAEMA) was prepared by batch and semi-continuous emulsion copolymerization. The effects of emulsifier type and concentration, polymerization temperature, and feed policy of emulsified monomers on process stability of the copolymerization and properties of the terpolymer latex were studied systematically. The results suggest that the selection of emulsifier should not be based on the HLB values for the DMAEMA-containing systems. The co-emulsifiers suitable for stabilizing the copolymerization process are in the order of SDS/OP>SDBS/OP>OT/OP. The results also indicate that an increase in amount of the co-emulsifiers, sodium dodecyl sulfate (SDS) and octyl phenol polyoxyethyl ether (OP), improves the process stability, decreases the surface tension and particle size of latices; however, it has little influence on the electrolyte stability when SDS/OP ratio is unchanged. A decrease in reaction temperature improves the process stability of polymerization but decreases the electrolyte stability of latices. The DMAEMA content does not affect the process stability significantly under investigated conditions but contributes to improve the electrolyte stability of latices. Compared to the batch polymerization process, the semi-continuous polymerization with a lower monomer feed rate provides better process stability for the polymerization and better electrolyte stability for the latices.

Study of Kinetic of Emulsion Copolymerization of Methyl Methacrylate/ethyl Acrylate

Emulsion polymerization of methyl methacrylate in concentration of emulsifiers below their CMCs—polymerization rate, particle size, and particle-size distribution

Seed Semicontinuous Emulsion Multi-Copolymerization of (meth)acrylates with High-Solid Content - Effect of the Operation Conditions

Preparation and Characterization of MMA-BA-DMAEMA Terpolymer Latex

Stability of Emulsion Copolymerization of Acrylic Monomers Containing Amino and Hydroxyl Groups

Stability of the emulsion copolymerization process of the latex containing glycidyl and amino groups

Study on Silicone Modified Polyurethane-Acrylate Copolymer Emulstion

Kinetics of Suspended Emulsion Polymerization of Methyl Methacrylate

Emulsion Copolymerization of Butyl Acrylate with Cationic Monomer Using Interfacial Redox Initiator System

Kinetics of methyl methacrylate and n-butyl acrylate copolymerization mediated by 2-cyanoprop-2-yl dithiobenzoate as a RAFT agent

Effects of Monomer Polarity on Mma/Ba/Nama Emulsifier-Free Emulsion Copolymerization

Kinetics of Styrene-Methyl Methacrylate Suspension-Emulsion Combined Polymerization

Study on Kinetics of Styrene/Butyl Acrylate/Crosslinker Emulsion Copolymerization

Emulsion copolymerization of MMA/BA in the presence of surface active monomers (II) - Kinetics and polymerization mechanism

Study on Kinetics of Vinyl Acetate/VeoVa 10 Emulsion Copolymerization

The effect of monomer polarity on MMA/BA/ Sodium methacrylate emulsifier-free emulsion copolymerization

Kinetics of N-Phenlymaleimide/Styrene/Acrylonitrile/ɑ-Methylstyrene Emulsion Copolymerization

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

Preparation of Mma-Ba-Dmaema Nanosized Latex

STUDY ON THE FORMATION MECHANISM OF MONODISPERSE PARTICLES IN THE EMULSIFIER-FREE EMULSION POLYMERIZATION OF METHYL METHACRYLATE AND BUTYL ACRYLATE

Stability Of Emulsifier-Free Emulsion Copolymerization Of Methyl Methacrylate/Butyl Acrylate/Sodium Mono(Ethyl Polyoxyethylene)Maleate