Abstract:Nanosilica particles well dispersed in ethanol were modified by 3-(trimethoxysilyl) propyl methacrylate (MPS) and then re-dispersed into methyl methacrylate (MMA) and poly(methyl methacrylate) matrix via a media replacement process and an in situ bulk polymerization process, respectively. The MPS modified status of silica particles and its effects on the dispersion of silica particles in different media and polymer matrix were systematically investigated by FTIR, TG, DLS and TEM. It was found MPS oligomer was the main form for MPS coupling on silica particles surface. Excessive MPS dosage not only resulted in the formation of MPS homo-polymeric particles in media phase, but also the MPS oligomer thick layer on silica surface, which would inevitably induce the small-scale aggregation of silica particles. There existed an appropriate MPS coupling amount for excellent silica dispersity, which is mainly related with the apparent coupling density of MPS molecules on silica particles surface. When the apparent coupling density is 1. 3 similar to 5. 6 mu mol . (m(2) . SiO2)(-1), the MPS coupling efficiency is acceptable and the modification of silica particles is sufficient. Only on this state, silica particles can be dispersed in the monomer and polymer matrix at the primary particles size level, even in the case of 20% silica content. The silica/monomer dispersion prepared via the above processes exhibited high silica dispersity, high silica content, high storage stability and high grafting controllability on silica surface. All of them imply that this kind of dispersion is avail to prepare silica/PMMA composite microspheres via in situ heterogeneous polymerization, and these microspheres would possess controllable morphology and controllable graft interface.

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Preparation of Poly(methyl Methacrylate)/ultrafine CaCO3 Composite Particles by In-Situ Dispersion Polymerization

In-Situ Heterogenous Polymerization of Methyl Methacrylateonto Nanometer Calcium Carbonate Particles

In Situ Polymerization of Poly(methyl Methacrylate)/clay Nanocomposites in Supercritical Carbon Dioxide

Preparation of Poly(Methylmethacrylate)/Layered Double Hydroxides Nanocomposites Via in Situ Solution Polymerization

Electrostatic Absorption of Initiator Onto Nanometer SiO2 Particles and In-Situ Emulsion Polymerization of Methyl Methacrylate in the Presence of Modified Nanometer SiO2

ANCHORING OF AZO INITIATOR AND GRAFTING OF POLY(METHYL METHACRYLATE) ONTO NANAOMETER SILICA

Particle Features of A Poly(Methyl Methacrylate) Resin Prepared by A New Emulsion Polymerization Process

Preparation and Characterization of Silica/Pmma Composites with Highly Dispersed Silica Nanoparticles Dispersion of Nanosilica in Mma

Synthesis and characterization of PMMA/Al2O3 composite particles by in situ emulsion polymerization

Preparation of PVC/CaCO3 Nano-Filler Composite Special for Building Material by In-Situ Polymerization

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

Preparation of Polymer–nanoparticle Composite Beads by a Nanoparticle-Stabilised Suspension Polymerisation

Preparation of Porous Pmma Resin by A New Emulsion Polymerization Process and the Mechanism of Particle Formation

Synthesis of Nanosize Poly(methyl Methacrylate) Microlatexes with High Polymer Content by a Modified Microemulsion Polymerization

Dispersion Catalytic Chain Transfer Polymerizations of Methyl Methacrylate in Supercritical Carbon Dioxide

Study on Poly(methyl Methacrylate)/carbon Nanotube Composites

Synthesis, Drug Absoprtion and Release Properties of Poly(methyl Methacrylate)/ Poly( 2-Hydroxyethyl Methacrylate) Composite Microspheres

Modification of Poly(vinyl Chloride) with Nano-CaCO3 Coated with Poly(methyl Methacrylate)

Facile Synthesis of Poly(methyl methacrylate) Silica Nanocomposite Monolith by In Situ Free Radical Polymerization of Methyl Methacrylate in the Presence of Functionalized Silica Nanoparticles

Compatibilization of poly(methyl methacrylate) and cellulose nanocrystals through co‐continuous phase to enhance the thermomechanical properties