Abstract:Methylmethacrylate copolymer nanoparticles with different hydrophilic chains were prepared by the free radical polymerization of methylmethacrylate with N-isopropylacrylamide (NIPAAm), N-methacrylic acid (MAA), N-trimethylaminoethylmethacrylate chloride (TMAEMC) or N-dimethylaminoethylmethacrylate hydrochloride (DMAEMC). These particles were characterized by particle size and zeta potential. The polymerization conditions were shown to influence the particle size and surface charge. Particle sizes of MMA–NIPAAm nanoparticles after 3h of reaction reached constant level at 180nm. An increasing amount of total monomer (0.5–5%) would result in the nanoparticles of particle size of 115–204nm for 30% NIPAAm of the total monomer. In the same range of 5–40% NIPAAm of the total monomer, the particle size decreased from 280 to 170nm. The concentration of the initiator APS up to a concentration of 0.2% for MMA–TMAEMC and 0.1% for MMA–NIPAAm showed no effect on the particle size of the final nanoparticle suspensions, while higher concentration would lead to aggregation in the polymerization process. MMA–NIPAAm nanoparticles were pH-dependent in zeta potential at pH 1–12 values reducing from 12.2mV to −16.8mV, respectively. Nanoparticles were incubated with pepsin and trypsin at 37°C for 20min and their enzyme inhibition was determined. The activity of pepsin decreased to 27% in the presence of MMA–NIPAAm nanoparticles, and MMA–MAA nanoparticles reduced the activity of trypsin to 39%, respectively.

In-Situ Heterogenous Polymerization of Methyl Methacrylateonto Nanometer Calcium Carbonate Particles

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Preparation of Poly(methyl Methacrylate)/ultrafine CaCO3 Composite Particles by In-Situ Dispersion Polymerization

Emulsion polymerization of methyl methacrylate in concentration of emulsifiers below their CMCs—polymerization rate, particle size, and particle-size distribution

ANCHORING OF AZO INITIATOR AND GRAFTING OF POLY(METHYL METHACRYLATE) ONTO NANAOMETER SILICA

In Situ Polymerization of Poly(methyl Methacrylate)/clay Nanocomposites in Supercritical Carbon Dioxide

Electrostatic Absorption of Initiator Onto Nanometer SiO2 Particles and In-Situ Emulsion Polymerization of Methyl Methacrylate in the Presence of Modified Nanometer SiO2

Polymerization of Methyl Methacrylate Using Organocalcium Compounds

Study on Suspension Graft Polymerization of MMA onto Nano-sized Basic Magnesium Chloride Whisker Surface in Methanol/Water Disperse Medium

In-Situ Bulk Polymerization of Dilute Particle/MMA Dispersions

Neutral Pd(II) and Ni(II) Acetylide Catalysts for the Polymerization of Methyl Methacrylate

Preparation of Poly(Methylmethacrylate)/Layered Double Hydroxides Nanocomposites Via in Situ Solution Polymerization

Dispersion Catalytic Chain Transfer Polymerizations of Methyl Methacrylate in Supercritical Carbon Dioxide

Synthesis of Methacrylate Macromonomers Using Silica Gel Supported Atom Transfer Radical Polymerization

Particle Features of A Poly(Methyl Methacrylate) Resin Prepared by A New Emulsion Polymerization Process

Preparation of Cross-Linked Microparticles of Poly(glycidyl Methacrylate) by Dispersion Polymerization of Glycidyl Methacrylate Using a PDMS Macromonomer As Stabilizer in Supercritical Carbon Dioxide

Polymerization of Methyl Methacrylate with Achiral 4B Group Metallocene Compounds

Preparation, characterization and enzyme inhibition of methylmethacrylate copolymer nanoparticles with different hydrophilic polymeric chains

Study of Kinetic of Emulsion Copolymerization of Methyl Methacrylate/ethyl Acrylate

SURFACTANT-FREE EMULSION POLYMERIZATION OF METHYL METHACRYLATE INITIATED BY Α-Methyl STYRENE-MALEIC ANHYDRIDE COPOLYMER MACROINITIATOR

Effect of Dispersed Polymeric Nanoparticles on the Bulk Polymerization of Methyl Methacrylate