Abstract:Nanosilica particles well dispersed in ethanol were modified by 3-(trimethoxysilyl) propyl methacrylate (MPS) and then re-dispersed into methyl methacrylate (MMA) and poly(methyl methacrylate) matrix via a media replacement process and an in situ bulk polymerization process, respectively. The MPS modified status of silica particles and its effects on the dispersion of silica particles in different media and polymer matrix were systematically investigated by FTIR, TG, DLS and TEM. It was found MPS oligomer was the main form for MPS coupling on silica particles surface. Excessive MPS dosage not only resulted in the formation of MPS homo-polymeric particles in media phase, but also the MPS oligomer thick layer on silica surface, which would inevitably induce the small-scale aggregation of silica particles. There existed an appropriate MPS coupling amount for excellent silica dispersity, which is mainly related with the apparent coupling density of MPS molecules on silica particles surface. When the apparent coupling density is 1. 3 similar to 5. 6 mu mol . (m(2) . SiO2)(-1), the MPS coupling efficiency is acceptable and the modification of silica particles is sufficient. Only on this state, silica particles can be dispersed in the monomer and polymer matrix at the primary particles size level, even in the case of 20% silica content. The silica/monomer dispersion prepared via the above processes exhibited high silica dispersity, high silica content, high storage stability and high grafting controllability on silica surface. All of them imply that this kind of dispersion is avail to prepare silica/PMMA composite microspheres via in situ heterogeneous polymerization, and these microspheres would possess controllable morphology and controllable graft interface.

Preparation of Polymer–nanoparticle Composite Beads by a Nanoparticle-Stabilised Suspension Polymerisation

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

A novel synthetic route to metal–polymer nanocomposites by in situ suspension and bulk polymerizations

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Preparation of Poly(Methylmethacrylate)/Layered Double Hydroxides Nanocomposites Via in Situ Solution Polymerization

Preparation of Polymer-Based Nano-Assembled Particles with Fe3O4 in the Core

Synthesis and characterization of PMMA/Al2O3 composite particles by in situ emulsion polymerization

Preparation of Bigger Core-Shell PS/PMMA Composite Particles by Suspension-Emulsion Combined Polymerization

Tailoring Emulsion Polymerization for High-Yield Synthesis of Tween 80 Stabilized Magnetic Cross-Linked Polystyrene Nanocomposite Particles

In situ and post-synthesis polymer stabilization of ferromagnetic nanoparticles synthesized by a membrane or conventional reactor

Effect of Surface Modification of Fe3O4 Nanoparticles on the Preparation of Fe3O4/polystyrene Composite Particles Via Miniemulsion Polymerization

Biomimic preparation of highly dispersible silica nanoparticles based polymer nanocomposites

Preparation of Crosslinked Composite Nanoparticles

Formation, Stabilization & Application of Polymeric Nanoparticles

In Situ Generation of Nanoparticles on and within Polymeric Materials

Preparation and Characterization of Silica/Pmma Composites with Highly Dispersed Silica Nanoparticles Dispersion of Nanosilica in Mma

Polymer-Fe3o4 Composite Janus Nanoparticles

Preparation of Self-Assembled Nanoparticle–Polymer Hybrids from Modified Silica Nanoparticles and Polystyrene-Block-Polyacrylic Acid Vesicles via the Co-Precipitation Method

In-Situ Bulk Polymerization of Dilute Particle/MMA Dispersions

In Situ Dispersion of Non-Aqueous Fe3O4 Nanocolloids by Microdroplet Coalescence and Their Use in the Preparation of Magnetic Composite Particles.

Preparation of Magnetic Hybrid Nanoparticles via Surface-Initiated Polymerization from Magnetite