Abstract:A new emulsion polymerization process, in which water acted as the dispersed phase and a mixture of methyl methacrylate (MMA) and cyclohexane acted as the continuous phase, was applied to the preparation of a poly(methyl methacrylate) (PMMA) resin. The primary (latex) particles were formed in the early stage of polymerization and coagulated as the polymerization conversion increased. Scanning electron micrographs showed that the final PMMA particles were porous and composed of loosely aggregated primary particles. The porosity characterized by cold di(2ethythexyl) phthalate absorption increased as the water/oil and cyclohexane/MMA mass ratios increased. The PMMA primary particles were smaller than the primary particles in the PMMA, resin prepared by suspension polymerization in the presence of cyclohexane. Because of the phase composition of the reaction system, the solubility of PMMA in a mixture of cyclohexane and MMA, and the particle morphology of PMMA, a particle formation mechanism, including the formation growth, and coagulation of primary particles in dispersed water droplets, was proposed. The primary particles formed mainly through a homogeneous nucleation mechanism and increased in size as MMA diffused from the oil phase to the water phase to the primary particles. The coagulation of the primary particles occurred because of the lower colloidal stability and the space limitations of the primary particles. (C) 2004 Wiley Periodicals, Inc.

Study on nano-size PMMA particles prepared by O/W microemulsion polymerization. - (1) Phase diagram, compatibilization and reaction kinetics

STUDY ON NANO-SIZE PMMA PARTICLES PREPARED BY O/W MICROEMULSION POLYMERIZATION --(Ⅰ) PHASE DIAGRAM, COMPATIBILIZATION AND REACTION KINETICS

Emulsion polymerization of methyl methacrylate in concentration of emulsifiers below their CMCs—polymerization rate, particle size, and particle-size distribution

Kinetics of Suspended Emulsion Polymerization of Methyl Methacrylate

Study of Kinetic of Emulsion Copolymerization of Methyl Methacrylate/ethyl Acrylate

Preparation of Bicontinuous Porous Polymeric Materials Via Microemulsion Polymerization

Particle Features of A Poly(Methyl Methacrylate) Resin Prepared by A New Emulsion Polymerization Process

Reversible addition–fragmentation chain transfer polymerization of methyl methacrylate in emulsion

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

Electrostatic Absorption of Initiator Onto Nanometer SiO2 Particles and In-Situ Emulsion Polymerization of Methyl Methacrylate in the Presence of Modified Nanometer SiO2

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Preparation of Porous Pmma Resin by A New Emulsion Polymerization Process and the Mechanism of Particle Formation

Study on Nano-Size PMMA Particles Prepared by O/W Microemulsion Polymerization —— Particle Diameter and Its Distribution, Molecular Weight and Microstructure of PMMA

Fundamental Study on Preparation Process and Structure Coutrol of PBA/PMMA

Effects of Monomer Polarity on Mma/Ba/Nama Emulsifier-Free Emulsion Copolymerization

The effect of monomer polarity on MMA/BA/ Sodium methacrylate emulsifier-free emulsion copolymerization

Preparation of Mma-Ba-Dmaema Nanosized Latex

Radiation-induced Polymerization of Methyl Methacrylate in Microemulsion with High Monomer Content

In-Situ Heterogenous Polymerization of Methyl Methacrylateonto Nanometer Calcium Carbonate Particles

Synthesis of Nanosize Poly(methyl Methacrylate) Microlatexes with High Polymer Content by a Modified Microemulsion Polymerization

Preparation of Bigger Core-Shell PS/PMMA Composite Particles by Suspension-Emulsion Combined Polymerization