Abstract:Lead zirconate titanate (PZT) ceramics were prepared by direct coagulation casting via high valence counterions (DCC–HVCI) using magnesium citrate as a coagulating agent assisted by the hydrolysis of glycerol diacetate. The colloidal behavior of PZT suspensions was evaluated by measuring the zeta potential and the viscosity. The dispersant content and solid loading were optimized to prepare concentrated PZT suspension. The results indicated that PZT suspension with solid loading up to 56vol% can be prepared by the addition of 0.5wt% ammonium polyacrylate at pH=10.6. The critical coagulation concentrations of magnesium and lead in 56vol% PZT suspensions are 15 and 35mM, respectively. The viscosity of 56vol% PZT suspensions with 0.5–1.0wt% magnesium citrate and 2vol% glycerol diacetate is higher than 30Pas at 60°C for 30min which is sufficient to coagulate the suspensions. The coagulating time is 60–90min at 50–70°C. The compressive strength of the coagulated wet samples decreases with the increase of coagulating temperature, but increases with the increase of magnesium citrate content. The strength is in the range 1.5–2.8MPa which is sufficiently high for demolding and handling without deformation. Dense PZT ceramics sintered at 1250–1280°C show homogeneous microstructures with relative densities of 99.2–99.7% and good piezoelectric properties compared with a traditional die pressing method.

Anti-crack machining of PZT ceramics for fabricating piezocomposites by using gelcasting technique

Application of Gelcasting to the Fabrication of Piezoelectric Ceramic Parts

Gelcasting of PZT

Rapid Prototyping of Piezoelectric Ceramics Via Selective Laser Sintering and Gelcasting

Gelcasting Based Solid Freeform Fabrication of Piezoelectric Ceramic Objects

Fabrication of Three-Dimensional Inter-Connective Porous Ceramics Via Ceramic Green Machining and Bonding

Water based gelcasting of lead zirconate titanate

Enhanced Piezoelectric Properties of PZT Ceramics Prepared by Direct Coagulation Casting Via High Valence Counterions (DCC–HVCI)

A Novel Approach to Improving the Electromechanical Properties of PZT-based Piezoelectric Ceramics Via a Grain Coating Modification Strategy

Fabrication of PZT microdevices using a high-yield sol-gel process

Microstructure and electrical properties of porous PZT ceramics with unidirectional pore channel structure fabricated by freeze-casting

Fabrication of complicated ceramic parts by gelcasting based on additive manufactured acetone-soluble plastic mold

Fabrication of Low Firing Piezoelectric Ceramics and Their Applications

Microstructure and Electrical Properties of Porous Pzt Ceramics Fabricated by Different Methods

Preparation and properties of piezoelectric composites of PZT/PVDF

Gelcasting of complex-shaped ZrB 2-SiC ultra high temperature ceramic components

Architectural Engineering Inspired Method of Preparing C-f/ZrC-SiC with Graceful Mechanical Responses

Processing and properties of porous PZT ceramics from particle-stabilized foams via gel casting

Porous PZT Ceramics with High Hydrostatic Figure of Merit and Low Acoustic Impedance by TBA-Based Gel-Casting Process

Microstructure and mechanical properties of ZrB2-SiC composites fabricated by the centrifugal gel casting

Mechanical Reinforcement and Piezoelectric Properties of Pzt Ceramics Embedded with Nano-Crystalline