Abstract:Lead zirconate titanate (PZT) ceramics were prepared by direct coagulation casting via high valence counterions (DCC–HVCI) using magnesium citrate as a coagulating agent assisted by the hydrolysis of glycerol diacetate. The colloidal behavior of PZT suspensions was evaluated by measuring the zeta potential and the viscosity. The dispersant content and solid loading were optimized to prepare concentrated PZT suspension. The results indicated that PZT suspension with solid loading up to 56vol% can be prepared by the addition of 0.5wt% ammonium polyacrylate at pH=10.6. The critical coagulation concentrations of magnesium and lead in 56vol% PZT suspensions are 15 and 35mM, respectively. The viscosity of 56vol% PZT suspensions with 0.5–1.0wt% magnesium citrate and 2vol% glycerol diacetate is higher than 30Pas at 60°C for 30min which is sufficient to coagulate the suspensions. The coagulating time is 60–90min at 50–70°C. The compressive strength of the coagulated wet samples decreases with the increase of coagulating temperature, but increases with the increase of magnesium citrate content. The strength is in the range 1.5–2.8MPa which is sufficiently high for demolding and handling without deformation. Dense PZT ceramics sintered at 1250–1280°C show homogeneous microstructures with relative densities of 99.2–99.7% and good piezoelectric properties compared with a traditional die pressing method.

Enhanced mechanical properties in Ag-particle-dispersed PZT piezoelectric composites for actuator applications

Sintering and Piezoelectric Properties of Co‐Fired Lead Zirconate Titanate/Ag Composites

Fabrication and Evaluation of PZT/Ag Piezoelectric Composites and Graded Actuator

Fabrication and Evaluation of PZT/Ag Composites and Functionally Graded Piezoelectric Actuators

Electrical and Mechanical Properties of Metal-Particle-Dispersed PZT-Matrix Composites

Enhanced Mechanical Behaviour of Lead Zirconate Titanate Piezoelectric Composites Incorporating Zinc Oxide Nanowhiskers

A Novel Approach to Improving the Electromechanical Properties of PZT-based Piezoelectric Ceramics Via a Grain Coating Modification Strategy

SINTERING AND ELECTRICAL AND MECHANICAL PROPERTIES OF LEAD ZIRCONATE TITANATE/SILVER PIEZOELECTRIC COMPOSITES

Research on the Flexural Property of Composite Laminates with Embedded PZT

Significantly Toughened PZT-based Piezoelectric Ceramics Simultaneously Keeping Excellent Electrical Properties Via Incorporating Trace Amount of Yttria-Partially-stabilized Zirconia

Electrical and Mechanical Properties of Piezoelectric Ceramic/Metal Composites in the Pb(Zr,Ti)O-3/Pt System

Enhanced Piezoelectric Properties of PZT Ceramics Prepared by Direct Coagulation Casting Via High Valence Counterions (DCC–HVCI)

Enhanced mechanical properties and excellent electrical properties of PZT piezoelectric ceramics modified by YSZ

Enhanced Piezoelectric and Mechanical Properties of Zno Whiskers and Sb2o3 Co-Modified Lead Zirconate Titanate Composites

Modified cofiring behaviors between PMN-PNN-PZT piezoelectric ceramics and PZT-doped 70Ag–30Pd alloy metallization

Mechanical and Electrical Properties of Small Amounts of In 2O3 Reinforced PZT Ceramics

Metal Particle Composite Hardening in Ba0.85Ca0.15Ti0.90Zr0.10O3 Piezoceramics

Mechanical and electrical properties of small amount of oxides reinforced PZT ceramics

High-field dielectric properties and high-power performance of Fe-modified PZN–PMS–PZT piezoelectric ceramics

Effect of ZnO Whisker Content on Sinterability and Fracture Behaviour of PZT Peizoelectric Composites

Fabrication and evaluation of PZT/Pt piezoelectric composites and functionally graded actuators