Effect of heat treatment on structure, magnetization and magnetostriction of Fe81Ga19 melt-spun ribbons

Jingjing Zhang,Tianyu Ma,Mi Yan

DOI: https://doi.org/10.1016/j.physb.2009.07.185

2009-01-01

Abstract:Structure, magnetization and magnetostriction of melt-spun Fe81Ga19 ribbons were investigated both before and after heat treatment. The matrix of melt-spun Fe81Ga19 ribbons kept a body-centered-cubic (bcc) structure (A2) at room temperature. [100] preferred orientation was formed during melt-spinning process and became stronger with the increase of the ribbon thickness. For the ribbons with a thickness of 110μm, maximum saturation magnetostrictive strain of −189ppm along ribbon length was obtained in the samples heat treated at 800°C for 3h and then quenched into water. This value was about 16% larger than that of melt-spun ones, which could be contributed to the single disordered A2 structure and the enhancement of [100]-oriented texture. However, when the ribbon samples were cooled at 2 and 0.5°C/min after heat treatment at 800°C for 3h, a minor quantity of ordered D03 and L12 phase was found to precipitate in the A2 matrix, respectively, which resulted in the reduction of both magnetization and magnetostrictive strain.