Magnetic force microscopy study of heat-treated Fe81Ga19 with different cooling rates

Jingjing Zhang,Tianyu Ma,Mi Yan

DOI: https://doi.org/10.1016/j.physb.2010.04.027

2010-01-01

Abstract:Phase constitution and domain structures of heat-treated Fe81Ga19 cooled from 800°C at different rates have been studied by X-ray diffraction (XRD) and magnetic force microscopy (MFM). Heat-treated samples were annealed at 800°C for 3h, followed by water quenching, air cooling (∼160°C/min), furnace cooling (∼5°C/min) and slow cooling (0.1°C/min). Both the as-quenched and air-cooled Fe81Ga19 had a single disordered bcc A2 phase, but exhibited obvious difference in alignment of stripe domains. Dendrite domains were observed in the furnace-cooled sample with the formation of the ordered D03 phase in the A2 matrix. For the slow-cooled Fe81Ga19 sample, L12 phase was found to be precipitated and showed a plate domain structure with a relatively weaker contrast. The great thermal history dependence of the initial domain structure of Fe81Ga19 samples is considered to be responsible for the change in their magnetostrictive behaviors.