High-temperature properties and enhanced magnetic properties by magnetic field heat treatment of D0 22 Mn 3− x Ga (x = 0, 0.2, and 0.4) alloys

Dong Liang,Guang Tian,Chao Yun,Hui Zhao,Shunquan Liu,Changsheng Wang,Jingzhi Han,Honglin Du,Qing Xu,Yan Zhang,Jinbo Yang,Wenyun Yang

DOI: https://doi.org/10.1063/5.0056030

IF: 4

2021-07-12

Applied Physics Letters

Abstract:<span><i>In situ</i> high-temperature XRD and magnetic field heat treatment (MFHT) under a magnetic field of 50 kOe have been used to investigate the structural and magnetic properties of the D0₂₂ Mn₃₋_<i>x</i>Ga (x = 0, 0.2, and 0.4). It was found that Mn₃₋_<i>x</i>Ga compounds maintain ferrimagnetic D0₂₂ phase in the temperature range of 300–700 K, and their magnetic properties were remarkably improved through MFHT. The saturation magnetization (<i>M</i>_s) of Mn_3.0Ga at 300 K increased by 37% from 18.3 to 25.0 emu/g after MFHT. All Mn_3-xGa samples showed superior thermal stability in magnetization from 300 to 500 K, and they still retained excellent magnetic properties at a temperature of up to 700 K. The magnetization of Mn_3.0Ga and Mn_2.8Ga showed a positive temperature coefficient from 300 to 400 K. Even at 700 K, <i>M_s</i> and <i>H_c</i> of 24.3 emu/g and 4.5 kOe were retained in Mn_2.8Ga, which is excellent for high-temperature applications. In addition, the coercivity mechanism of Mn₃₋_<i>x</i>Ga at 700 K was illustrated by minor hysteresis loops measurement, and it was found that the coercivity mechanism of Mn₃₋_<i>x</i>Ga at 700 K was dominated by the pinning mechanism.</span>

physics, applied