Mössbauer Investigation of Magnetostrictive Fe83Ga17 with Trace Rare- Earth Doping
P. S. Stamenov,Y. He,C. Jiang,M. Coey
DOI: https://doi.org/10.1109/intmag.2018.8508629
2018-01-01
Abstract:Fe-Ga alloys (Galfenol) are known to exhibit an unusually large magneto- striction, of order 320 ppm, which is attributed to the presence of nanoscale tetragonal Ga-rich $\mathrm {L}6 _{0}$ inclusions embedded in the bcc A2 Fe-rich matrix solid solution. The tetragonal axis in a particular nanoinclusion is determined by the orientation of nearest-neighbour Ga-Ga pairs. The distribution of these axes parallel to the three {100}directions means that the maximum magnetostriction can be achieved in a single crystal when the magnetic field is applied parallel to any cube edge. More recently it has been shown that traces of rare-earth atoms, $\approx 0.1$ at. %, which can be incorporated into these alloys when they are rapidly cooled, can greatly increase the magnetostric- tion by a factor of 2 – 3 [1]–[3]. The mode of action of the trace dopants has yet to be determined. Here we employ Mössbauer spectroscopy in an attempt to gain some insight into the location and mode of action of the trace rare earth dopants. The samples were produced by melt spinning. Precursor ingots of Fe 83 Ga 17 M x , with $\mathrm {M}=$ La, Nd, Sm, Tb and Tm and $x =0$, 0.05 or 0.25 were first prepared from 4N pure Fe and Ga by arc melting under argon four times and annealed at $1000 ^{o}\mathrm {C}$ in Ar to ensure homogeneity. The ingots were then melt spun on a copper wheel with a surface velocity of 20 ms $^{-1}$, to obtain ribbons about $50 \mu \mathrm {m}$ thick, and 5 mm wide. Transverse magnetostriction was measured by the strain gauge method in the direction of the ribbon length, with the field applied perpendicular to the plane of the ribbon. A field of up to 2 T was used to saturate the magnetization. Mössbauer spectra were obtained at room temperature in a conventional constant acceleration spec- trometer with a source of 57 Co in Rh. The spectrum of undoped Fe 83 Ga 17 is shown in Figure 1, together with associated fit to six hyperfine components [3]. It is composed of two main broad overlapping components with hyper- fine fields of 31.2 and 26.9 T, associated with iron in the A2 phase with 0 or 1 Ga neighbours [3]–[5]. They constitute 87 % of the total spectral area, and their ratio is 66:34, compared to a ratio 37:63 expected for a purely random distribution of Ga in the bcc phase. The Ga concentration in A2 on this basis should be 4.8 %, and the remainder is therefore Ga-rich. We identify two minor components with the tetragonal nanoinclusions, which make up 4.8 % of the total volume. One typical example of a doped sample, with 0.5 % La is shown in Figure 2. The sum of the spectra of iron with 0 and I Ga neighbours again represents 87 % of the total area, but the ratio to rises to 68:32, and the amount of iron in the tetragonal nanoinclusions rises to 5.6 % of the total. These are small changes, but they are observed systematically in spectra with five different rare earth dopants. We can therefore conclude that the rare earths serve to increase the volume of nanoinclusions in the sample, and they increase the amount of Ga present in the nanoinclusions. A second conclu- sion from the data is that there is no significant difference between the 0.05 % and 0.25 % doping, when they are measured for the same dopant. This shows that the solubility limit for the rare earth in these melt-spun ribbons is below 0.05 %. The conclusions are consistent with electron microscopy observations. We consider that the rare-earth dopant is probably initially incorporated into the nanoinclusions and it enhances their tetragonality up to the metastable solubility limit, which is less than 0.05 %. Beyond that, there is no further effect and the rare earth probably precipitates out in a 2:17 or 1:2 phase. In this way we can understand the strong influence of very small amounts of rare earth doping on the magnetostriction of Fe 83 Ga 17 .