Dislocation Structure of Non-Habit Plane of Α Precipitates in a Ti–7.26 Wt.% Cr Alloy

F Ye,WZ Zhang

DOI: https://doi.org/10.1016/j.actamat.2005.10.017

IF: 9.4

2005-01-01

Acta Materialia

Abstract:The dislocation structures of edge facet and end face of proeutectoid α precipitates in a β matrix in a Ti–7.26 wt.% Cr alloy were studied using transmission electron microscopy. Two sets of dislocations, which are parallel to the dislocations on the habit plane of the α plate, were observed on the edge facet. The spacing of one set of coarse-spaced dislocations is about 9.4nm. Their Burgers vector is [100]β([2−1−10]α/3) determined by g·b contrast analyses. The spacing of the other set of fine-spaced dislocations is about 1.8nm. Their Burgers vector possibly is [111]β/2([11−20]α/3). A dislocation network on the end face is formed by the dislocations on the habit plane and edge facet looping around the α plate. Another set of dislocations was observed on the end face at intersections between the dislocations on the habit plane and the coarse-spaced dislocations on the edge facet. Their Burgers vector possibly is [11−1]β/2([2−1−1−3]α/6). Based on the observations, a three-dimensional model of the dislocation structure of the α plate was constructed.