Abstract:This article reports the field emission measurements on as grown tetrahedral amorphous carbon (ta-C) and nitrogen incorporated tetrahedral amorphous carbon (ta-C: N) films grown using a pulsed filtered cathodic vacuum arc technique. The effect of varying thickness on field emission in the as grown ta-C films and the effect of varying nitrogen content in ta-C: N films have also been studied. The values of threshold field of emission (Eturnon) increase with decrease of thickness in the as grown ta-C films. Nitrogen incorporation up to 5.2at.% in ta-C films decreases the value of Eturnon from 9.9to5.1V∕μm and thereafter it starts increasing again. To understand the mechanism of electron emission, a realistic energy band diagram of ta-C:N∕n++Si heterojunction has been proposed from the experimentally measured valence and conduction band offsets, using in situ x-ray photoelectron spectroscopy and optical spectroscopy data already published in DRM 9 (2000) 1148. The data are explained using the Fowler and Nordheim theory. The field emission results obtained reveal that there exists a barrier to emission and the main barrier is at the front surface and this is related to the conduction band offset of the ta-C:N∕n++Si heterojunction.

Electron Emission from Amorphous Carbon Film on Discontinuous Ag Islands

Electron Emission from Pd-Carbon Compound Film on Carbon Nanoislands

Electron Field Emission Studies from Amorphous Carbon Thin Films

A Field Emission Study of the Critical Parameters of Amorphous Carbon Films Deposited on a Variety of Carbonaceous Substrates

Study on Multifractal Spectrum of Semicontinuous Ag Films

Field emission from a new form of thin film amorphous carbon having nanoparticle inclusions and carbon nanotubes

Field emission from Nanocomposite Carbon

Nitrogen Containing Hydrogenated Amorphous Carbon for Thin-Film Field Emission Cathodes

Electron emission from carbon film on island-like tin oxide layer

Field Emission from As Grown and Nitrogen Incorporated Tetrahedral Amorphous Carbon/Silicon Heterojunctions Grown Using A Pulsed Filtered Cathodic Vacuum Arc Technique

Field Electron Emission from Carbon Containing Thin Films

Electron Emission from Discontinuous Gold-Carbon Compound Film on Etched Porous Aluminum Oxide

Field Electron Emission From Individual Carbon Nanotubes Of A Vertically Aligned Array

Self-texturing of nitrogenated amorphous carbon thin films for electron field emission

Modeling of the Electron Field Emission Process in Polycrystalline Diamond and Diamond-Like Carbon Thin Films

Modelling of the Electron Field Emission Process in Polycrystalline Diamond-Like Carbon Thin Films

Stable Field Emission with Low Threshold Field from Amorphous Carbon Films Due to Layer-by-layer Hydrogen Plasma Annealing

The Intrinsic Relation Between Field Electron Emission and Structure Characteristics of Amorphous Diamond Film

A Study of Field Electron Emission Phenomenon Associated with Amorphous Diamond Thin Films

Low Field-Induced Electron Emission Phenomenon Observed from the Carbon Containing Thin Films

Hot electron field emission via individually transistor-ballasted carbon nanotube arrays.