Abstract:Temperature is one of the critical factors that strongly affect the behavior of hydrogen isotopes in tungsten (W). This work investigates the effect of initial exposure temperature on the deuterium (D) retention and surface blistering in recrystallized W. D plasma exposure is started at 420 K and 600 K, respectively, and then changed to the same temperature of 520 K. For each temperature, the irradiation fluence is ∼ 1 × 1026 D m−2, and therefore the total fluence is ∼ 2 × 1026 D m−2 for each sample. A reference W sample was also exposed at 520 K with the same total fluence. Compared with the reference sample, it is found that the initial temperature of 420 K significantly inhibits the formation of intergranular blisters and leads to a reduction of intragranular blisters in size. Although the initial temperature of 600 K facilitates the formation of intergranular blisters, the intergranular blister size is reduced. This is possibly related to the relatively higher concentration of trapped D over a large depth range as revealed by the TMAP simulation results, leading to the fact that intergranular cracks are more prone to propagate along sloping grain boundaries. Thermal desorption spectra results show that the initial exposure temperature of 420 K and 600 K reduce D retention by a factor of ∼ 56 % and ∼ 34 %, respectively. It is considered to be connected with the blistering-induced defects and D transport in W, which are strongly affected by the initial exposure temperature. This work demonstrates that the initial exposure temperature plays a crucial role in D behavior in W, improving the understanding of the temperature effects of hydrogen isotopes behavior in W.

Hydrogen Blister Formation on Cold-Worked Tungsten with Layered Structure

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Nucleation Mechanism of Intra-Granular Blisters in Tungsten Exposed to Hydrogen Plasma

Hydrogen Behaviors at the Near-Surface Region of Tungsten: A First-Principles Study

Blistering on Tungsten Surface Exposed to High Flux Deuterium Plasma

Irradiation hardening induced by blistering in tungsten due to low-energy high flux hydrogen plasma exposure

Growth Mechanism of Subsurface Hydrogen Cavities in Tungsten Exposed to Low-Energy High-Flux Hydrogen Plasma

Effect of thickness on the blistering of tungsten exposed to deuterium plasma

Surface Blistering and D Desorption in High-Energy-rate Forging W, W-Y2O3, W-TiC Exposed to Deuterium Plasma

Mechanisms of helium irradiation blistering and surface deformation in tungsten

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Deuterium Distribution and Behavior of Blisters in Pre-Damaged and Undamaged Tungsten

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Surface morphology and deuterium retention in tungsten exposed to high flux D plasma at high temperatures

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Effect of initial exposure temperature on the deuterium retention and surface blistering in tungsten

Blistering and retention behavior of laser powder bed fused tungsten alloys under hydrogen plasma irradiation

Deuterium-induced Nanostructure Formation on Tungsten Exposed to High-Flux Plasma

Helium Radiation Blistering Mechanisms in Tungsten: Ion Channeling Effects

Micron-Bubble Formation on Polycrystal Tungsten Due to Low-Energy and High-Flux Helium Plasma Exposure

Influence of Nitrogen Pre-Irradiation at Different Temperatures on Surface Blistering and Deuterium Retention in Tungsten