Abstract:In this work, we reported that the fibrous silica nanosphere, also called as KCC-1, was facilely synthesized by the improved microemulsion hydrothermal fabrication strategy. The obtained KCC-1 was investigated as the support of the Ni based catalysts toward CO2 methanation. The obtained catalysts with unique dendrimeric mesopore structure and outstanding structural properties could provide easily accessible as well as highly dispersed Ni nanoparticles to the gaseous reactants. Besides, the Ni based catalysts with commercial SiO2 and MCM-41 as supports were also prepared as the reference catalysts to demonstrate the advantages of the dendrimeric mesoporous channels. Various techniques, such as X-ray powder diffraction (XRD), N-2 physisorption, transmission electron microscopy (TEM), H-2 temperature programmed reduction (H-2-TPR), CO2 temperature programmed desorption (CO2-TPD), X-ray photoelectron spectroscopy (XPS), etc., were used to characterize the catalytic supports and corresponding catalysts. It was found that the metallic Ni nanoparticles could be highly dispersed over the catalysts supported on fibrous KCC-1 with dendrimeric mesoporous channels. Furthermore, the catalytic performances toward CO2 methanation had been further evaluated over these catalysts at different temperatures. It was found that the KCC-1 supported catalyst performed much higher low-temperature catalytic activities than the reference catalysts supported on commercial SiO2 and MCM-41, suggesting that the fibrous and dendrimeric mesoporous channels displayed distinctive advantages by accommodating enough metallic Ni active sites. The kinetic study also revealed that the topology of the mesoporous channel could obviously influence the apparent activation energy in the CO2 methanation reaction. Besides, the temperature programmed surface reaction (TPSR) and in-situ Diffused Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS) of the CO2 methanation were also carried out to reveal the possible reaction pathway and mechanism. We also found that the fibrous silica nanosphere (KCC-1) supported catalyst demonstrated much better sintering-proof property of the metallic Ni nanoparticles than the reference catalysts during the 40 h stability tests at 400 degrees C. Therefore, the present fibrous silica nanosphere (KCC-1) could be considered as the promising support for Ni based catalysts toward CO2 methanation.

Low temperature fabrication of hollow carbon nanospheres over Ni/Al2O3 by the catalytic method

The Production of Carbon Nano-Onions and Wheat Stalk Nano-Chains over Stainless Steel Supported La0.95mg0.05ni0.8co0.2o3 Catalyst

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

In Situ Carbon Nanotube Synthesis by the Reduction of NiO/γ-Al2O3 Catalyst in Methane

Hierarchical hollow Ni/γ-Al2O3 catalyst derived from flower-like Ni-Al layered double hydroxide with stable catalytic performance for CO2 methanation

Mesoporous Carbon Materials with Ultra‐Thin Pore Walls and Highly Dispersed Nickel Nanoparticles

Nanosized Aluminum Nitride Hollow Spheres Formed Through a Self-Templating Solid–gas Interface Reaction

Synthesis of Thin-Walled Carbon Nanotubes from Methane by Changing the Ni/Mo Ratio in a Ni/Mo/MgO Catalyst

Fabrication of Carbon-Coated Aluminum Nanoparticles and Carbon Quantum Dots by Thermal Plasma in Liquid Nitrogen Environment

Preparation of Nanosized Iron Catalyst and Small Diameter Carbon Nanotubes from Methane Decomposition

A low temperature organic synthesis of monodispersed NiRu nanocrystals for CO 2 methanation

Three-dimensional porous Mn–Ni/Al2O3 microspheres for enhanced low temperature CO hydrogenation to produce methane

Self-templated synthesis of polycrystalline hollow aluminium nitride nanospheres

Effect of adding nickel to iron–alumina catalysts on the morphology of as-grown carbon nanotubes

Constructing Highly Dispersed Ni Based Catalysts Supported on Fibrous Silica Nanosphere for Low-Temperature CO2 Methanation

Synthesis of Carbon Nanospheres with Small Diameterby Microwave Pyrolysis of Methane Directly

Large-Scale Synthesis of Herringbone Carbon Nanofibers on Nonsupported Nickel Catalyst

Nanocatalysts Anchored on Nanofiber Support for High Syngas Production Via Methane Partial Oxidation

Synthesis of Carbon Nanotubes by Catalytic Chemical Vapor Deposition over Methane Reduced Ni Catalyst

Formation of carbon nanofibers/nanotubes by chemical vapor deposition using Al2O3/KOH

Low Temperature Synthesis Of High-Density Carbon Nanotubes On Insulating Substrate