Abstract:Starting from bismuth, tellurium and selenium chunks, n-type Bi2Te3−xSex (x ⩽ 0.3) alloys were obtained by melt spinning (MS) combined with a resistance pressing sintering (RPS) process. The phases, microstructures and compositions of the samples were evaluated by x-ray diffraction, field emission scanning electron microscopy, and energy dispersive x-ray spectroscopy during each step in the preparation process, respectively. The influences of Se doping, MS and RPS processes on the thermoelectric (TE) properties of Bi2Te3−xSex alloys were investigated in detail. The Bi2Te3−xSex powders could be well compacted by the RPS process and the relative densities of the bulks prepared by RPS were all higher than 96%. The partially oriented lamellar structure could be observed at some regions of the samples prepared by RPS, and the monolayer thickness of the lamellar structure in the MS-RPS samples was smaller than that in the smelting-RPS sample. The MS process was confirmed as an excellent method to obtain fine microstructures and low lattice thermal conductivity for the TE materials. All evidence about electrical and thermal transport properties suggested that suitably increasing the Se content could effectively improve the ZT value. The maximum ZT value of 0.84 was obtained for the Bi2Te2.7Se0.3 prepared by MS-RPS at 423 K. As opposed to the conventional hot pressing and spark plasma sintering, the RPS method introduced here is more suitable for practical industrial application due to its cost saving and high efficiency.

Preparation of AgxPbmSbTe2+m-Based Thermoelectric Materials by MA-SPS Method and Evaluation of Their Thermoelectric Properties

Enhanced thermoelectric performance of n -type PbTe bulk materials fabricated by semisolid powder processing

Composition Optimization of P-Type AgSn M SbTe M +2 Thermoelectric Materials Synthesized by Mechanical Alloying and Spark Plasma Sintering

High-performance Ag0.8Pb18+xSbTe20 Thermoelectric Bulk Materials Fabricated by Mechanical Alloying and Spark Plasma Sintering

AgPbSbTe Thermoelectric Materials Fabricated by Mechanical Alloying and Spark Plasma Sintering(SPS)

Fabrication and Property of High-Performance Ag-Pb-Sb-Te System Semiconducting Thermoelectric Materials

Fine-grained Lead-Free P-Type AgSn 4 SbTe 6 Thermoelectric Materials Synthesized by Mechanical Alloying and Spark Plasma Sintering

Powder Metallurgic Synthesis of Mid-Temperature Lead-Free Agsn18sbte20 Thermoelectric Materials and Processing Influence on Thermoelectric Performance

Comparison of Thermoelectric Performance of AgPbxSbTe20 (x=20–22.5) Polycrystals Fabricated by Different Methods

Fast Preparation of AgxPb20SbTe20 (x = 0.5–3) Component with High Thermoelectric Performance

ChemInform Abstract: Composition Optimization of P‐Type AgSnmSbTem+2 Thermoelectric Materials Synthesized by Mechanical Alloying and Spark Plasma Sintering.

Thermoelectric Properties of Bi2Te3 Alloy Prepared by Mechanical Alloying and Spark Plasma Sintering

Research Progress on Processing of Thermoelectric Materials by Mechanical Alloying Combined with Spark Plasma Sintering

Thermoelectric Performance of AgPb X SbTe 20 ( X = 17 to 23) Bulk Materials Derived from Large-Particle Raw Materials

Improved Thermoelectric Properties of Bi2Te3−xSexalloys by Melt Spinning and Resistance Pressing Sintering

Enhanced Thermoelectric Performance of Mg-Doped AgSbTe 2 by Inhibiting the Formation of Ag 2 Te

Mechanically Enhanced P- and N-Type Bi2Te3-based Thermoelectric Materials Reprocessed from Commercial Ingots by Ball Milling and Spark Plasma Sintering

Thermoelectric enhancement at low temperature in nonstoichiometric lead-telluride compounds

Maximizing Thermoelectric Performance of AgPbmSbTem+2 by Optimizing Spark Plasma Sintering Temperature

Thermoelectric performance enhancement of Pb-doped α -MgAgSb near room temperature

High Thermoelectric Performance of p-Type Bi0.4Sb1.6Te3+ x Synthesized by Plasma-Assisted Ball Milling