Transport and Tem on Dysprosium Metallofullerene Peapods

D. Obergfell,J. C. Meyer,M. Haluska,A. N. Khlobystov,S. Yang,L. Fan,D. Liu,S. Roth

DOI: https://doi.org/10.1002/pssb.200669117

2006-01-01

Abstract:Single‐walled carbon nanotubes (SWNTs) produced by the arc‐discharge method using non‐magnetic catalysts were filled with Dy@C82 endohedral metallofullerenes. Transport measurements were performed on (Dy@C82)@SWNT metallofullerene peapod samples in field‐effect transistor configuration at 4.2 K. After the transport investigations the substrates were partially etched away enabling us to take TEM images of the very same metallofullerene peapod samples on which transport had been carried out before. This procedure gives essential information on whether the sample measured was a single tube or a bundle and on the degree of tube filling. In the case of the presented measurements, TEM investigations revealed one sample to be a metallofullerene peapod bundle and another one to be an individual tube being not or not completely filled despite of a high overall sample filling. Both samples behave as semiconductors, where the latter sample exhibits Coulomb blockade oscillations for low bias voltages. Thus we present the first combined Coulomb blockade diamond and TEM measurements on a single nanotube and moreover the first transport data including the transfer characteristics I sd(V g) of a sample which is confirmed to be a metallofullerene peapod bundle. (© 2006 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)