Abstract:The Ti-based bulk metallic glasses (BMG) with high Ti content (>50 at.%) have attracted wide attention for their outstanding mechanical properties, despite their glass forming ability (GFA) is still relatively poor. Here the (Ti55Zr15Be20Ni10)(100-x)Cu-x(x = 2, 4, 6, 8 and 10 at.%) BMGs were designed and prepared by copper mold casting. The critical diameter of the original alloy could be enhanced from 5 mm to 10 mm with the Cu addition of 4 at.%, which is the first reported centimeter-sized Ti-based BMG with Ti content more than 52 at.%. In addition, all the as-prepared BMGs exhibited higher yield strength (above 2000 MPa). And the supercooled liquid range of the as-prepared Ti-based BMGs were enlarged from 35 K to 74 K by Cu addition. Electrochemical measurements showed that the BMGs with Cu addition of 0-6 at.% exhibited much higher pitting potentials (over 573 mV/SCE) than that of 304 stainless steel (304SS) in 3.5 wt% NaCl aqueous solution. And The XPS analysis revealed that the Cu addition might lead to the enrichment of Cu and the deficiency of Ti, Zr, Ni elements in passive film, which could induce the worse corrosion resistance of the Ti-based BMGs with high Cu content. The results indicate that the developed Ti-based BMGs possess good GFA, mechanical properties and corrosion resistance. (C) 2017 Elsevier B.V. All rights reserved.

Effects of additional noble elements on the thermal stability and mechanical properties of Cu–Zr–Al bulk glassy alloys

Effect of Al addition on properties of Cu45Zr45.5Ti9.5 bulk metallic glass

Cu-Based Bulk Glassy Alloys with Good Mechanical Properties in Cu-Zr-Hf-Ti System

High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems

Effects of Al on Glass-Forming Ability and Thermal Stability of Cu-Based Metallic Glass

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

Cu-based bulk glassy alloys with high tensile strength of over 2000 MPa

Mechanism of Ag and Al on improving the glass forming ability of CuZr-based alloys

Effects of minor addition of Al and Ag elements on the atomic structure and mechanical property of ZrCu-based metallic glasses

Ti Microalloying Effect on Corrosion Resistance and Thermal Stability of CuZr-based Bulk Metallic Glasses

Cu-alloying Effect on Crystallization Kinetics of Ti41Zr25Be28Fe6 Bulk Metallic Glass

Formation, Structure, and Crystallization Behavior of Cu-Based Bulk Glass-Forming Alloys

Effects of Cu Addition on the Glass Forming Ability and Corrosion Resistance of Ti-Zr-Be-Ni Alloys

Effect of Ti addition on properties of Zr54Al10.2Ni9.4Cu26.4 glass forming alloy

Effect of Ag substitution for Ti on glass-forming ability, thermal stability and mechanical properties of Zr-based bulk metallic glasses

The effect of minor alloying on the glass forming ability and crystallization reaction of Ti32.8Zr30.2Cu9M5.3Be22.7 (M=Fe, Co, and Ni) bulk metallic glass

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

The Correlation among the Atomic Structure, Electronic Valence Band and Properties of Zr-Cu-Al-Ag Bulk Metallic Glasses

Unusual Solidification Behavior of a Zr–Cu–Ni–Al Bulk Glassy Alloy Made from Low-Purity Zr

Glass Forming Ability and Crystallization of Zr–Cu–Ag–Al–Be Bulk Metallic Glasses

Cu-Zr-Al-Ti bulk metallic glass with enhanced glass-forming ability, mechanical properties, corrosion resistance and biocompatibility