Effects of the proportion of ultrafine diamond and zirconia on the flexural strength of core resin

LUO Juan,LIU Xue-heng,WANG Xin-zhi

DOI: https://doi.org/10.3969/j.issn.1006-673X.2007.05.001

2007-01-01

Abstract:Objective To observe the influence of adding two particle size zirconia and ultrafine diamond into the photocurable composite resin on the flexural strength.Methods Different content of nano-zirconia or micro-zirconia and ultrafine-diamond(UFD),mixed with main filler barium glass,was added into resin matrix to fabricate photocurable composite core materials,then the flexural strength of the materials was measured.Results After 2wt%,3.5wt% and 5wt% nano-zirconia or micro-zirconia was respectively added into the composite mixture of 60wt% barium and 0.2wt% UFD,the flexural strength changed significantly and the 3.5wt% group was the highest.After 0wt%,2wt%,3.5wt%,5wt% nano-zirconia were respectively added into the composite mixture of 70wt% barium and 0.1wt% UFD,the flexural strength also changed significantly and the 2wt% group was the highest.Conclusion The flexural strength of the core resin made of special content of zirconia and UFD can reach the corresponding National and ISO criteria,which could meet the clinical requirements.