Abstract:Background: Clinical practitioners may have become familiar with the rapid transformation of dental composites. However, they may not scientifically understand the factors influencing the mechanical and physical properties. Scientific knowledge of filler-resin interaction can significantly improve clinical understanding of resin composites. Several independent studies have examined the mechanical and physico-mechanical properties of dental resin composites; however, no comprehensive study has examined the influence of fillers and resin materials on the physico-mechanical properties of both self-cure and dual-cure composites. Methods: This study performed investigations on the physico-mechanical behaviour of four commercially available dual-cure dental composites (Bioactive, Fill Up!, Surefil One, Cention N) and two commercially available self-cure dental composites (Stela Capsule and Stela Automix). Test specimens for flexural and compressive strength, microhardness, fracture toughness, and hydrolytic behaviour were prepared and tested as per respective standards. The data sets were statistically analysed using one-way ANOVA and Tukey's post-hoc comparison. Results: There was a substantial variation in flexural strength and modulus values in this study, ranging from 32.0 to 113.4 MPa and 2.36 to 12.07 GPa, respectively. Similarly, there were significant differences in compressive strength between the materials in this study, ranging from 119.3 to 223.5 MPa. The highest fracture toughness value was found to be 1.41 MPa.m0.5, while the lowest value was 0.43 MPa.m0.5. Variations in surface microhardness were significant (24.11-68.0 N/mm2), which correlated with the filler content. Water sorption and solubility demonstrated high variations among materials, with Surefil One exceeding ISO 4049 thresholds significantly. Conclusions: A linear correlation can be established between surface microhardness (HV) and flexural and compressive moduli, as well as filler content (wt.%). However, both flexural and compressive strengths are impacted by the resin's constituent monomers and the resin-filler matrix's cross-linking capability. Additionally, factors such as filler size, shape, and the cross-linking ability of the resin-filler matrix play a crucial role in fracture toughness and the propagation of cracks within the restoration. Also, resin monomers and filler particle size affect the hydrolytic degradation characteristics of composites, which can also affect their mechanical properties. © 2023 Australian Dental Association.

Effect of water storage on the flexural properties of three dual-cure core buildup composite resins

Effect of Water Storage on Mechanical Property of Dual-Cured Resin Cements with Different Irradiations

[Influence of Long-Term Water Storage on the Physical and Chemical Properties of Four Different Dental Cements].

Polymerization efficacy of composite resin cores with different fluidities under short-time super-intense light exposures

Surface morphology and mechanical properties of conventional and self-adhesive resin cements after aqueous aging.

Volumetric dimensional change of six direct core materials

Water absorption in artificial composites: Curse or blessing?

Effect of polymerisation protocols on water sorption, solubility and hygroscopic expansion of fast-cure bulk-fill composite

Effect of curing mode of resin composite cements on water sorption, color stability, and biaxial flexural strength

The Investigation of Flexural Strength Properties of Resin Composite Core Materials

The influence of hygroscopic expansion of resin supporting dies on the fracture resistance of ceramic restorations during thermal cycling

The effect of long-term water storage on the resin adhesive interface between dentine and glass ceramic

Comparative analysis of self-cure and dual cure-dental composites on their physico-mechanical behaviour

Nanoindentation creep: The impact of water and artificial saliva storage on milled and 3D-printed resin composites

Comprehensive Evaluation of Long-Term Dentin Bond Strength, Water Sorption, Solubility, and Degree of Conversion of Self-Adhesive Resin Composites

Bottom/top hardness ratio and dentin bonding stability of conventional and bulk-fill resin composites

Effects of the proportion of ultrafine diamond and zirconia on the flexural strength of core resin

Impact of Fast High-Intensity versus Conventional Light-Curing Protocol on Selected Properties of Dental Composites

Effect of Hydrothermal Aging on the Flexural Strength and Microhardness of Materials Used for Additive or Subtractive Manufacturing of Definitive Restorations

Mechanical properties of dual-polymerizing resin-core material, dual-polymerizing resin cement, and bulk-fill composite resin used for restoring endodontically treated teeth

Influence of curing mode on polymerization of dual cured flowable resin composites