Abstract:Recent advances in dental resin based restorative materials have given rise to development of composites for bulk placement, to replace the need for incremental layering. Clinical consequences of microleakage are secondary caries, pulp inflammation, marginal discoloration, postoperative sensitivity, and the longevity of filling. Surface hardness is one of the mechanical properties of the restoration that should always be taken into account, particularly when they are faced with large areas of heavy masticatory forces. Accordingly, the current study was conducted to investigate the effect of packing technique and curing time on the marginal sealing and surface hardness of two bulk fill resin composites.Standardized class II proximal box cavities were prepared on the mesial and distal surface of the selected premolar teeth with the total of 48 cavities. The prepared cavities were randomly divided into 2 main groups, 24 cavities each, according to the placement technique used for cavity restoration either placement of bulkfill single increment of 4 mm depth or incremental placement of two increments of 2 mm each. Each group was subdivided into 2 subgroups, 12 cavities each, according to the bulk fill composite resin used; X-trafil bulkfill composite and Quixfil bulkfill composite. These subgroups were then subdivided into two smaller groups, 6 cavities each, according to the curing times either curing for 10 seconds following the manufacturers’ instructions or curing for 20 seconds. For all specimens, after bonding procedures, bulk-fill resin composites were manipulated and applied in cavities as the previously assigned methodology, specimens were then immersed in 2% methylene blue dye for 24 hours. Teeth were sectioned and viewed under a binocular stereomicroscope. Readings were recorded.A total of 80 cylindrical resin composite specimens were prepared. samples were divided into 4 groups according to the type of bulk fill composite (X-tra fil or Quixfil) and irradiation time (10s or 20s). The resin composite was applied in the mold, covered with mylar strips and light cured using LED light curing unit with an intensity of 1200mW/cm2. Vickers Microhardness tester was used with microindentation carried out using a load of 500g. Three readings for each surface were taken and an average reading was calculated. X-trafil bulkfill composite showed significantly lower degree of leakage than Quixfil bulkfill composite. No significant difference in microleakage was shown between different curing times nor different application techniques. X-trafil bulkfill composite showed significantly higher microhardness than Quixfil bulkfill composite Curing for 10 seconds showed significantly higher microhardness. Bulk-fill single increment of 4 mm recorded significantly higher microhardness value. Within the limitations of the current study, we can conclude that 4-mm bulk fill packing of bulkfill composite resin, cured for 10 seconds, had adequate marginal sealing performance. Surface microhardness of bulkfill composite resin packed at 4-mm bulk fill, cured for 10 seconds, is acceptable.

Effect of polymerisation protocols on water sorption, solubility and hygroscopic expansion of fast-cure bulk-fill composite

Diversity of short-term DC outcomes in bulk-fill RBCs subjected to a 3 s high-irradiance protocol

Impact of Fast High-Intensity versus Conventional Light-Curing Protocol on Selected Properties of Dental Composites

Thermography and conversion of fast-cure composite photocured with quad-wave and laser curing lights compared to a conventional curing light

Polymerization and shrinkage kinetics and fracture toughness of bulk-fill resin-composites

Effect of curing mode of resin composite cements on water sorption, color stability, and biaxial flexural strength

Effect of High-radiant Emittance and Short Curing Time on Polymerization Shrinkage Vectors of Bulk Fill Composites

Physico-mechanical characteristics of commercially available bulk-fill composites

Post-curing in dental resin-based composites

The effect of light curing intensity on bulk-fill composite resins: heat generation and chemomechanical properties

The Effect of Bulk Depth and Irradiation Time on the Surface Hardness and Degree of Cure of Bulk-Fill Composites

Monomer conversion, microhardness, internal marginal adaptation, and shrinkage stress of bulk-fill resin composites

Effect of Radiant Exposure on the Physical and Mechanical Properties of 10 Flowable and High-viscosity Bulk-fill Resin Composites

Monomer elution and shrinkage stress analysis of addition-fragmentation chain-transfer-modified resin composites in relation to the curing protocol

Effects of light-curing modes on the polymerization shrinkage and surface hardness of composite resins]

Degree of Conversion and Polymerization Shrinkage of Bulk-Fill Resin-Based Composites.

The Effect of Two Different Light-Curing Units and Curing Times on Bulk-Fill Restorative Materials

Effect of water storage on the flexural properties of three dual-cure core buildup composite resins

Mechanical Properties of Bulk-Fill Resin Composites with Single Increment Up to 4 Mm: A Novel Mechanical Strength Test

Polymerization shrinkage of light-cured conventional and bulk-fill composites -The effect of cavity depth and post-curing

Effect of packing technique and curing time on the marginal sealing and surface hardness of two bulk-fill resin composites