Abstract:In this work, BaTiO3 powders were synthesized by molten-salt synthesis method using BaCO3, TiO2, and the eutectic salts (NaCl-KCl) as the raw materials. A systematic study indicating the effects of calcination temperature as well as the molar ratio of NaCl to KCl in the mixed salt with respect to BaCO3-TiO2 on the microstructures of BaTiO3 powders is reported. The results showed that all the powders crystallized in a tetragonal perovskite structure, as confirmed by X-ray diffraction pattern and Raman spectra. With increasing the calcination temperature, the morphology of the as-prepared BaTiO3 powders developed from rectangular/spherical aggregates to circular or cubic shapes and the average particle size was also increased from 320 nm to 900 nm. With increasing the molar ratio of BaCO3: TiO2: NaCl: KCl, the average particle size was slightly decreased from 440 nm to 360 nm, and the morphology of the as-synthesized BaTiO3 powders transformed from rectangular and cubic shapes to sphere shapes. The chemical compositions of the as-synthesized BaTiO3 powders obtained from energy dispersive X-ray analysis are in agreement with the nominal ratios. The present results provide a generalized methodology to large-scale synthesize other perovskite transitional metal oxide powders with controllable sizes and shapes. (C) 2016 Elsevier B.V. All rights reserved.

A Simple Molten Salt Method to Synthesize Single-Crystalline Potassium Titanate Nanobelts

Large-Scale Synthesis of Sodium and Potassium Titanate Nanobelts

Molten Salt Synthesis of Single-Crystalline K2ti6o13 Annular Nanostructures

Synthesis of Single-Crystalline Barium Tetratitanate Nanobelts Via Self-Sacrificing Template Process

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

Synthesis of Single-Crystalline Barium Dititanate Nanobelts

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Key to Enhance Thermoelectric Performance by Controlling Crystal Size of Strontium Titanate

Composition and shape control of single-crystalline Ba1-xSrxTiO3 (x=0-1) nanocrystals via a solvothermal route

Hydrothermal Synthesis and Characterization of Single-Crystal Lead Titanate Nanoflakes

Bi4Ti3O12 nanocrystals synthesized via hydrothermal reaction

Molten-salt Synthesis of BaTiO3 Powders and Their Atomic-Scale Structural Characterization

A single-source molten salt synthesis of uniform octahedral Na2Ti3O7 particels composed of nanorods

Fabrication and Activity Enhancement of Nano-Photocatalyst Films by Molten Salt Treatment

Enlarging the application of potassium titanate nanowires as titanium source for preparation of TiO 2 nanostructures with tunable phases

Large-scale Synthesis of Nanocrystals of Barium Titanate and Other Titanates Through Solution-Phase Processes

Hydrothermal Synthesis of Single-Crystalline Perovskite PbTiO3 Nanosheets with Dominant (001) Facets

Mechanism of the formation, growth and transformation of BaTi2O5 nanorods synthesized by one-step in molten-salts

Synthesis of K6ta10.8o30 Nanowires by Molten Salt Technique

Synthesis of Ti powders with different morphologies via controlling the valence state of the titanium ion in KCl-NaCl molten salt

Synthesis and Characterization of Ion-Exchangeable Titanate Nanotubes