Abstract:Single-crystalline perovskite BaTiO3 (BTO) nanorods were synthesized by (BaTi2O5-template) molten salt synthesis (MSS) methods. The effects of process parameters (eg, calcination temperature, reaction time, molten salt content, as well as different phase structures of TiO2 and barium oxides) on the formation of BTO nanorods and their structural characteristics were systematically investigated. The BTO nanorods synthesized at 800 degrees C for 5 hours by MSS method with the molar salt ratios of BaCO3:TiO2 (anatase):NaCl:KCl equal to 1:1:60:60, exhibited smooth and clean surfaces through their lengths. Their diameters were in the range of 130-200 nm with average length of 5 mu m. Large-scale amount of BTO nanorods was synthesized by BaTi2O5-template MSS method at 650 degrees C with molar salt ratios of BaC2O4:BaTi2O5 (template):NaCl:KCl equal to 1:1:60:60. The BTO nanorods successfully retained the one-dimensional morphology of the BaTi2O5 templates and their lengths were in the range of 5-10 mu m with an average diameter of similar to 300 nm. The single-crystalline nature of individual BTO nanorod was revealed by its selected area electron diffraction patterns and high-resolution TEM images. The BTO nanorods exhibited good optical properties with optical bandgaps in the range of 2.5-2.6 eV. Such optical bandgaps make the present BTO nanorods promising candidates for ferroelectric photovoltaic devices. Dielectric properties of the BTO nanorods synthesized by MSS method were comparatively investigated with the BTO nanorods synthesized by the BaTi2O5-template MSS method. It is found that the later BTO nanorods exhibit better dielectric properties and their synthesized temperature is also much lower than the former ones.

Molten Salt Synthesis of Single-Crystalline K2ti6o13 Annular Nanostructures

A Simple Molten Salt Method to Synthesize Single-Crystalline Potassium Titanate Nanobelts

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Hydrothermal Synthesis and Microstructure of Self-Assembled 3D Flower-Like K2Ti6O13 Nanostructure

Heterogeneous 3D Morphological Evolution of Ni Microparticles in Molten Salts: Visualized by Operando Synchrotron X-ray Nano-tomography

A single-source molten salt synthesis of uniform octahedral Na2Ti3O7 particels composed of nanorods

Synthesis of Ti powders with different morphologies via controlling the valence state of the titanium ion in KCl-NaCl molten salt

Synthesis of Single-Crystalline Barium Tetratitanate Nanobelts Via Self-Sacrificing Template Process

Mesoporous-Structure-Tailored Hydrothermal Synthesis And Mechanism Of The Srtio3 Mesoporous Spheres By Controlling The Silicate Semipermeable Membranes With The Koh Concentrations

Surfactant-Free Fabrication of Catio3 Butterfly-Like Dendrite Via A Simple One-Step Hydrothermal Route

Synthesis of K6ta10.8o30 Nanowires by Molten Salt Technique

Hydrothermal synthesis of flower-like SrCO3 nanostructures

Molten-salt Synthesis of BaTiO3 Powders and Their Atomic-Scale Structural Characterization

Hydrothermal Reaction Mechanism and Pathway for the Formation of K2Ti6O13 Nanowires

Strain-Induced Formation of K2ti6o13 Nanowires Via Ion Exchange

Mechanism of the formation, growth and transformation of BaTi2O5 nanorods synthesized by one-step in molten-salts

Molten Salt Synthesis of BaTiO3 Nanorods: Dielectric, Optical Properties, and Structural Characterizations

Black Composites Photocatalyst Coatings of K2ti6o13-Tio2/Tic with Nano-Sheet Flower-Like Structure by Heat Treatment in Molten Salt

Synthesis of ZnO Nano-crystal Powder by Molten Salt Method

Fabrication and Activity Enhancement of Nano-Photocatalyst Films by Molten Salt Treatment

Synthesis and characterization of K2Ti6O13 nanowires