Abstract:Single-crystalline perovskite BaTiO3 (BTO) nanorods were synthesized by (BaTi2O5-template) molten salt synthesis (MSS) methods. The effects of process parameters (eg, calcination temperature, reaction time, molten salt content, as well as different phase structures of TiO2 and barium oxides) on the formation of BTO nanorods and their structural characteristics were systematically investigated. The BTO nanorods synthesized at 800 degrees C for 5 hours by MSS method with the molar salt ratios of BaCO3:TiO2 (anatase):NaCl:KCl equal to 1:1:60:60, exhibited smooth and clean surfaces through their lengths. Their diameters were in the range of 130-200 nm with average length of 5 mu m. Large-scale amount of BTO nanorods was synthesized by BaTi2O5-template MSS method at 650 degrees C with molar salt ratios of BaC2O4:BaTi2O5 (template):NaCl:KCl equal to 1:1:60:60. The BTO nanorods successfully retained the one-dimensional morphology of the BaTi2O5 templates and their lengths were in the range of 5-10 mu m with an average diameter of similar to 300 nm. The single-crystalline nature of individual BTO nanorod was revealed by its selected area electron diffraction patterns and high-resolution TEM images. The BTO nanorods exhibited good optical properties with optical bandgaps in the range of 2.5-2.6 eV. Such optical bandgaps make the present BTO nanorods promising candidates for ferroelectric photovoltaic devices. Dielectric properties of the BTO nanorods synthesized by MSS method were comparatively investigated with the BTO nanorods synthesized by the BaTi2O5-template MSS method. It is found that the later BTO nanorods exhibit better dielectric properties and their synthesized temperature is also much lower than the former ones.

Mechanism of the formation, growth and transformation of BaTi2O5 nanorods synthesized by one-step in molten-salts

Process, Fundamental and Application of One-Step Molten-Salt Synthezed BaTi2O5 Nanorods

Molten Salt Synthesis of BaTiO3 Nanorods: Dielectric, Optical Properties, and Structural Characterizations

Morphology transformation of barium titanate nanostructures in molten salt medium

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

A Simple Molten Salt Method to Synthesize Single-Crystalline Potassium Titanate Nanobelts

Molten-salt Synthesis of BaTiO3 Powders and Their Atomic-Scale Structural Characterization

Microstructural Characterization and Dielectric Properties of Single Crystalline BaTi2O5 Nanowires Prepared by Molten-Salt Method

Efficient synthesis of single-crystalline Na2Ti6O13 nanoribbons

Composition and shape control of single-crystalline Ba1-xSrxTiO3 (x=0-1) nanocrystals via a solvothermal route

Morphological Control of Ba-Ti-O Particles Prepared by Molten Salt Synthesis

A single-source molten salt synthesis of uniform octahedral Na2Ti3O7 particels composed of nanorods

Key to Enhance Thermoelectric Performance by Controlling Crystal Size of Strontium Titanate

Molten salt synthesis of rod-like tungsten bronze niobate particles

Synthesis of mesoporous strontium titanate by molten salt assisted template-free method

Synthesis of K6ta10.8o30 Nanowires by Molten Salt Technique

Synthesis of Single-Crystalline Barium Tetratitanate Nanobelts Via Self-Sacrificing Template Process

Synthesis of K0.5Bi0.5TiO3 Powders by Molten Salt Method

Nonaqueous sol–gel synthesis and growth mechanism of single crystalline TiO2 nanorods with high photocatalytic activity

Synthesis of Pure Brookite Nanorods in a Nonaqueous Growth Environment

Molten salt route of single crystal barium titanate nanowires