Abstract:In this work, BaTiO3 powders were synthesized by molten-salt synthesis method using BaCO3, TiO2, and the eutectic salts (NaCl-KCl) as the raw materials. A systematic study indicating the effects of calcination temperature as well as the molar ratio of NaCl to KCl in the mixed salt with respect to BaCO3-TiO2 on the microstructures of BaTiO3 powders is reported. The results showed that all the powders crystallized in a tetragonal perovskite structure, as confirmed by X-ray diffraction pattern and Raman spectra. With increasing the calcination temperature, the morphology of the as-prepared BaTiO3 powders developed from rectangular/spherical aggregates to circular or cubic shapes and the average particle size was also increased from 320 nm to 900 nm. With increasing the molar ratio of BaCO3: TiO2: NaCl: KCl, the average particle size was slightly decreased from 440 nm to 360 nm, and the morphology of the as-synthesized BaTiO3 powders transformed from rectangular and cubic shapes to sphere shapes. The chemical compositions of the as-synthesized BaTiO3 powders obtained from energy dispersive X-ray analysis are in agreement with the nominal ratios. The present results provide a generalized methodology to large-scale synthesize other perovskite transitional metal oxide powders with controllable sizes and shapes. (C) 2016 Elsevier B.V. All rights reserved.

Synthesis of Single-Crystalline Barium Dititanate Nanobelts

Synthesis of Highly Dispersed Barium Titanate Nanoparticles by a Novel Solvothermal Method

Synthesis of Single-Crystalline Barium Tetratitanate Nanobelts Via Self-Sacrificing Template Process

Molten salt route of single crystal barium titanate nanowires

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Preparation of A Monodispersed Suspension of Barium Titanate Nanoparticles and Electrophoretic Deposition of Thin Films

Composition and shape control of single-crystalline Ba1-xSrxTiO3 (x=0-1) nanocrystals via a solvothermal route

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

A Simple Molten Salt Method to Synthesize Single-Crystalline Potassium Titanate Nanobelts

Large-scale Synthesis of Nanocrystals of Barium Titanate and Other Titanates Through Solution-Phase Processes

Size-controlled synthesis of BaTiO3 nanocrystals via a hydrothermal route

Preparation and Characterization of Monodispersed BaTiO3 Nanocrystals Using One-Step Solvothermal Method

New Nonhydrolytic Route to Synthesize Crystalline BaTiO3 Nanocrystals with Surface Capping Ligands

Molten-salt Synthesis of BaTiO3 Powders and Their Atomic-Scale Structural Characterization

Direct Synthesis of Ultrafine Tetragonal BaTiO3 Nanoparticles at Room Temperature

Morphology transformation of barium titanate nanostructures in molten salt medium

Barium Titanate Tetragonal Prism Arrays: Preparation and Characterization

Low-temperature synthesis of barium titanate thin films by nanoparticles electrophoretic deposition

Process, Fundamental and Application of One-Step Molten-Salt Synthezed BaTi2O5 Nanorods

Fabrication of Highly Dispersed Crystallized Nanoparticles of Barium Strontium Titanate in the Presence of N,N-dimethylacetamide

Unusual Reuniting of Barium Titanate Nanoparticles