Study on Properties of Cyanate Ester Resin Modified by Epoxy Silane

李倩,颜红侠,王倩倩,王艳丽

DOI: https://doi.org/10.3969/j.issn.1004-2849.2010.09.001

2010-01-01

Abstract:The influences of epoxy silane(ESi) contents on mechanical properties and dynamic mechanical properties of ESi/BCE(bisphenol A-dicyanate ester resin) system were investigated by ESi as modifier of BCE.The results showed that the toughness and strength of BCE could be obviously increased by appropriate ESi content.The modified BCE/ESi system had best mechanical properties because the impact strength was increased from 10.1 kJ/m2 to 14.49 kJ/m2,and the flexural strength was increased from 94.11 MPa to 110.94 MPa respectively when the mass fraction of ESi was 6%.It was the main reason for toughness increase that the crosslinker density of ESi/BCE system was reduced to an appropriate value.The glass transition temperature(Tg) of ESi/BCE system was less than that of pure BCE system,but its decreasing amplitude was smaller.