Abstract:Isothermal oxidation of microcrystalline Ni–11.5Cr–4.5Co–0.5Al (wt%) superalloy sheet fabricated by electron beam physical vapor deposition (EB-PVD) at 900°C in air was investigated. Mass gain curves were obtained on testing the alloy in dry air. And characterization of the surface morphology and cross-sections was performed on samples isothermally oxidized for different exposure times. Surfaces and cross-sections of the oxidized specimens were studied by scanning electron microscopy (SEM). Phase identification of the oxide scale was performed by glancing angle X-ray diffraction (GAXRD) and energy dispersive X-ray microanalysis (EDX). The experiment results indicated that the oxidation kinetics of microcrystalline Ni–11.5Cr–4.5Co–0.5Al superalloy sheet follows a cubical power law at initial oxidation stage and fourth power law for long oxidation terms. The oxide scales consisted mainly of a mixed oxide at initial oxidation stage and a double-layer scale with an outer NiO oxide layer, and inner mixed oxides exposed for long terms at 900°C. The fine oxide grains could be formed on microcrystalline superalloy surface. Taking the short circuit diffusion through grain boundaries into account, an oxidation kinetic with cubical power law in mixed oxide and fourth power law in single-phase oxide were derived. And the excellent fitting of the present model to the experimental data was obtained. The results suggested that the growing oxide layer of microcrystalline Ni–11.5Cr–4.5Co–0.5Al superalloy sheet, which controlled the ionic transportation, contained mainly mixed oxide at initial oxidation stage and the scale/substrate interface single-phase oxide for long terms.

Study on the Microstructure of Nicocral Sheet Deposited by Eb-Pvd at 800 Degrees C

Microstructure Evolution of Electron Beam Physical Vapour Deposited Ni-23.5Cr-2.66Co-1.44Al Superalloy Sheet During Annealing at 600 °C

Preparation and Mechanical Properties of Ni-Cr-Al Alloy by Eb-Pvd

B22-P-17Evolution of the MC Carbide in Nickel-base Single Crystal Superalloy Exposing at 950 °C

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Oxidation Behaviors of NiCrCoAl Superalloy Sheet Prepared by EB-PVD at 1000℃

Research on Microstructure of Ni-20.3Cr-4.6Co-2.1Al As-deposited State Sheet Prepared by EB-PVD

Mechanical Properties and Oxidation Formation of Eb-Pvd Deposited Ni-Cr-Al Alloy

Cyclic oxidation behaviour of as-deposited Ni-11·5Cr-4·5Co-0·5Al superalloy sheet when heated at 800°C

Preparation and Mechanical Properties of Nicocraly/Nicr Laminates by Electron Beam Physical Vapor Deposition

Oxidation Kinetics of Microcrystalline Ni–11.5Cr–4.5Co–0.5Al Superalloy Sheet Fabricated by Electron Beam Physical Vapor Deposition at 900 °C

Oxidation Kinetics of Microcrystalline Ni-11.5Cr-4.5Co-0.5Al Superalloy Sheet Fabricated by Electron Beam Physical Vapor Deposition at 800 °C

Microstructures and mechanical properties of a NI-CR-AL alloy by EB-PVD

Microstructure of As-Deposited Ni-Cr-Al Alloy Thin Sheet by EBPVD

Effect of Cr on solidification structure and microhardness of Al-Ni alloy

Oxidation Kinetics Of Microcrystalline Ni-11.5cr-4.5co-0.5a1 Superalloy Sheet Fabricated By Electron Beam Physical Vapor Deposition At 800 Degrees C

Structures and mechanical properties of Ni-Co-Cr based superalloy prepared by technique of EB-PVD

Oxidation behaviours of electron beam physical vapour deposition fabricated microcrystalline Ni–23·5Cr–2·66Co–1·44Al superalloy sheet at 1000°C

Evaluation of EB-PVD Deposited Ni–Cr–Al Alloy Foil

The Isothermal Oxidation Behaviors of As-Deposited and Heat-Treated Ni–11.5Cr–4.5Co–0.5Al Sheet by EB-PVD at 800°C

Microstructure and Properties of Ni-Based Superalloy Sheet Prepared by Eb-Pvd