Microstructure evolution behavior of Ni3Al (γ′) phase in eutectic γ-γ′ of Ni3Al-based alloy

Jian Ding,Shan Jiang,Yanmo Li,Yuting Wu,Jing Wu,Yuanyi Peng,Xin He,Xingchuan Xia,Chong Li,Yongchang Liu
DOI: https://doi.org/10.1016/j.intermet.2018.04.010
IF: 4.075
2018-07-01
Intermetallics
Abstract:Based on its excellent high-temperature performances, polycrystalline Ni3Al-based alloys have attracted more and more attention. In this work, different thermal cycle aging treatments (TCAT) were applied to investigate microstructure evolution behavior of Ni3Al (γ′) phase in eutectic γ-γ′ area of JG4246A alloy. SEM equipped with energy dispersive X-ray spectrometer (EDS) and high-resolution transmission electron microscopy (HRTEM) were used for microstructure observation and mechanism analysis. The results showed that plate-like Ni3Al (γ′) phase and twinning Ni3Al (γ′) formed in eutectic γ-γ′ area due to its initial state of the alloy and thermal cyclic aging treatment conditions. Meanwhile, blocky Ni3Al (γ′) phase precipitated along eutectic γ-γ′ area and dual phase (γ+γ′) area ((γ-γ′)/(γ+γ′)) interfaces. Vacancies and dislocations generated during short-term TCAT were responsible for the formation of plate-like Ni3Al (γ′) phases in eutectic γ-γ′ area of as-cast alloy. While, for the solution-treated alloy, dislocations and internal stress generated during long-term TCAT led to the formation of twinning Ni3Al (γ′) in eutectic γ-γ′ area and blocky Ni3Al (γ′) phase along (γ-γ′)/(γ+γ′) interface.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?