Preparation, Characterization and Electrochemical Properties of Mesoporous LiFe0.99Mo0.01PO4/C

Chunyang Yu,Zhongli Wang,Yu Chen,Dingguo Xia,Wangsheng Chu,Ziyu Wu

DOI: https://doi.org/10.1007/s12598-009-0062-y

IF: 6.318

2009-01-01

Rare Metals

Abstract:A mesoporous LiFe 0.99 Mo 0.01 PO 4 /C composite was synthesized by the sol-gel method using (NH 4 ) 2 MoO 4 as a doping starting material. The formation of conductive carbon, metal doping and mesopores was achieved simultaneously in the prepared material. The characterizations of crystal structures and microstructures were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), extended X-ray-absorption fine-structure (EXAFS) and X-ray-absorption near-structure spectroscopy (XANES), while the surface area was determined using N 2 adsorption techniques. Cyclic voltammetry (CV) and charge-discharge cycling performance were used to characterize its electrochemical properties. The sample possessed uniformly distributed mesopores with an average pore size of 4 nm, and the specific surface area was about 69.368 m 2 /g. The results show that the reversible capacity of mesoporous LiFe 0.99 Mo 0.01 PO 4 /C is about 160 mAh/g at 0.1C, 135 mAh/g at 1C and 90 mAh/g at 5C, respectively. The capacity fading is neglectable.