Abstract:The LiMnxFe1-xPO4/C (x = 0.5, 0.6, and 0.7) cathode materials for lithium-ion batteries were synthesized by polyethylene glycol (PEG) 400 as the carbon source via a combination of wet ball-milling and high-temperature solid-state reaction. The analysis results of X-ray diffraction (XRD), scanning electron microscopy (SEM), and high-resolution transmission electron microscopy (HRTEM) indicate that the as-prepared LiMn0.6Fe0.4PO4/C sample has a single-phase orthorhombic olivine structure, and the majority of particle sizes range from 100 to 200 nm with a ~2-3 nm carbon coating layer. The electrochemical measurements demonstrate that the obtained LiMn0.6Fe0.4PO4/C composite possesses preferable Li-ion storage properties, and the discharge capacity of 137.7 mAh g-1 at 1 C rate, which is 83.6% of that at 0.1 C rate. The composite also exhibits outstanding cycling stability, with a capacity retention of 98.2% after 100 cycles at 0.2 C rate. And the differential capacity analysis (dQ/dV) reveals that the dominating degradation of LiMn0.6Fe0.4PO4/C is caused by the Mn2+ /Mn3+ redox capacity loss which is located at ~4.12/3.96V, whether during the charge or discharge process. Moreover, the LiMn0.6Fe0.4PO4/C sample delivers excellent high-temperature performances (45 °C), with improved reversible capacity and capacity retention of 148.7 mAh g-1 and 99.3% after 80 cycles at 0.5 C rate, respectively.

The Preparation and Characterization of LiFe<sub>0.98</sub>Ni<sub>0.01</sub>Nb<sub>0.01</sub>PO<sub>4</sub>/C by Carbon Reduction Route

The preparation and characterization of LiFe0.98Ni0.01Nb0.01PO4/c by carbon reduction route

The Preparation and Characterization of LiFe<sub>0.98</sub>Mn<sub>0.02</sub>PO<sub>4</sub>/C by Spray-Drying and Low Temperature Reduction Route

The preparation and characterization of LiFe0.98Mn0.02PO4/C by spraydrying and low temperature reduction route

Olivine LiFePO4 Nanocrystallites Embedded in Carbon-Coating Matrix for High Power Li-ion Batteries

Synthesis, characterization and properties of LiFePO4/C cathode material

Synthesis of LiFePO<sub>4</sub>/C by Carbon Thermal Reduction Method and Its Electrochemical Properties

A Novel Synthesis and Characterization of LiFePO4 and LiFePO4/C As a Cathode Material for Lithium-Ion Battery

Characterization and Electrochemical Properties of LiFePO<SUB>4</SUB>/C Composite with Carbon Core Structure: Characterization and Electrochemical Properties of LiFePO<SUB>4</SUB>/C Composite with Carbon Core Structure

Preparation and Electrochemical Properties of High-performance LiFePO_4

Preparation, Characterization and Electrochemical Properties of Mesoporous LiFe0.99Mo0.01PO4/C

Preparation of the Particle Size Controllable LiFePO4/C and Its Electrochemical Profile Characterization

LiFePO<sub>4</sub>/C Cathode Materials Prepared by One-Step Fast Carbothermal Method Using Fe<sub>2</sub>O<sub>3</sub> as Raw Materials

Preparation and Electrochemical Performance of LiFePO_4/C Using Fe_2O_3 As Raw Material

Synthesis and electrochemical performances of carbon-coated and Ni-doped LiFePO4 anode materials

Optimized Performances of Core–shell Structured LiFePO4/C Nanocomposite

Preparation and Electrochemical Properties of Carbon-Coated LiMn0.6Fe0.4PO4 Cathode Material for Lithium-Ion Batteries

Synthesis and electrochemical characterization of LiFePO4/C Cathode materials for Li-ion batteries

A Novel Nano Structured LiFePO4/C Composite As Cathode for Li-ion Batteries

Electrochemical Performance of LiFe1−xVxPO4/carbon Composites Prepared by Solid-State Reaction

Preparation and properties of LiFePO4/C composite materials with Fe2O3 as starting reactant

The Preparation and Characterization of LiFe&lt;sub&gt;0.98&lt;/sub&gt;Ni&lt;sub&gt;0.01&lt;/sub&gt;Nb&lt;sub&gt;0.01&lt;/sub&gt;PO&lt;sub&gt;4&lt;/sub&gt;/C by Carbon Reduction Route