Synergetic Effect of the Crystallinity, Particle Size of LiFePO4 and the In-Situ Introduced Fe2P on Its High-Rate Capability
MingXia GAO,HongGe PAN,YongFeng LIU,Xin YE,JunHua WANG
DOI: https://doi.org/10.1360/972013-793
2013-01-01
Chinese Science Bulletin
Abstract:LiFePO4/C composite with high crystallinity, sub-micron particle size and suitable content of in-situ introduced Fe2P was synthesized by a sol-gel method, in which LiOH, Fe2C2O4 and NH4H2PO4 were used as starting materials, and ethylene glycol was used as complexing agent and carbon source. The precursor of LiFePO4 was calcined at a comparatively low temperature for relatively long time combined a following calcination at a comparatively high temperature for relatively short time. The composite shows high-rate capability as cathode material for lithium-ion batteries. The structure and the electrochemical properties of the LiFePO4/C composites synthesized by different calcination parameters were analyzed by X-ray diffraction, scanning electron microscopy, element analysis and electrochemical testing of galvanostatic charge-discharge, etc. The results show that the step-wise calcination at different temperatures for different times is an effective approach to obtain suitable amount of in-situ Fe2P, control the particle size and enhance the crystallinity of LiFePO4, which results in a significant improvement in the high-rate capability of LiFePO4. The LiFePO4/C composite synthesized at a calination temperature of 600℃ for 20 h followed by a further calcination at 700℃ for 4 h has 4wt% Fe2P and 3wt% C. The composite possesses discharge capacities of 140, 110 and 100 mAh/g at discharge rates of 1, 10 and 20 C, respectively.