Synthesis of nano FePO 4 and electrochemical characterization of composite cathode material LiFePO 4/C
WU Yu-Ling,PU Wei-Hua,REN Jian-Guo,JIANG Chang-Yin,WAN Chun-Rong
DOI: https://doi.org/10.3724/SP.J.1077.2012.00422
IF: 1.292
2012-01-01
Journal of Inorganic Materials
Abstract:Nano FePO4 center dot xH(2)O powders were synthesized by controlled crystallization method, using Fe(II) compound as the iron source. The nano FePO3 center dot xH(2)O powders were pretreated at 500 degrees C for 4 h in air to obtain nano FePO4 precursor. Then the olivine nano LiFePO4/C composites were obtained through carbonthermal reduction process at different temperatures. The structure, morphology, physicochemical properties and electrochemical properties of the nano FePO4 center dot xH(2)O powder, FePO4 precursor and LiFePO4/C composites synthesized at different temperatures were characterized in detail by thermogravimetric/differential scanning calorimeter (TG/DSC), X-ray diffraction (XRD), scanning electron microscope (SEM), Brunauer-Emmett-Teller (BET) surface area measurement and electrochemical measurement. The result show that the nano LiFePO4/C composite calcined at 700 degrees C for 10 h has fine particle sizes of about 40-100 nm. The BET test shows that the as-prepared nano LiFePO4/C composite has great specific surface area of 79.8 m(2)/g. The nano LiFePO4/C composite cathode material can deliver an initial discharge capacity of 156.5, 134.9, 105.8, 90.3 and 80.9 mAh/g in the voltage range of 2.5-4.2 V, at rate of 0.1C, 1C, 5C, 10C and 15C respectively, which exhibits good rate performance. The nano LiFePO4/C composite also demonstrates excellent cyclic performance.