Abstract:A joint chemical reactor system referred to as an ultrasonic-intensified micro-impinging jetting reactor (UIJR), which possesses the feature of fast micro-mixing, was proposed and has been employed for rapid preparation of FePO4 particles that are amalgamated by nanoscale primary crystals. As one of the important precursors for the fabrication of lithium iron phosphate cathode, the properties of FePO4 nano particles significantly affect the performance of the lithium iron phosphate cathode. Thus, the effects of joint use of impinging stream and ultrasonic irradiation on the formation of mesoporous structure of FePO4 nano precursor particles and the electrochemical properties of amalgamated LiFePO4/C have been investigated. Additionally, the effects of the reactant concentration (C=0.5, 1.0 and 1.5molL−1), and volumetric flow rate (V=17.15, 51.44, and 85.74mLmin−1) on synthesis of FePO4·2H2O nucleus have been studied when the impinging jetting reactor (IJR) and UIJR are to operate in nonsubmerged mode. It was affirmed from the experiments that the FePO4 nano precursor particles prepared using UIJR have well-formed mesoporous structures with the primary crystal size of 44.6nm, an average pore size of 15.2nm, and a specific surface area of 134.54m2g−1 when the reactant concentration and volumetric flow rate are 1.0molL−1 and 85.74mLmin−1 respectively. The amalgamated LiFePO4/C composites can deliver good electrochemical performance with discharge capacities of 156.7mAhg−1 at 0.1C, and exhibit 138.0mAhg−1 after 100 cycles at 0.5C, which is 95.3% of the initial discharge capacity.

Electrochemical Performance of LiFePO 4 /(c+fe 2 P) Composite Cathode Material Synthesized by Sol-Gel Method

Rapid Preparation of High Electrochemical Performance LiFePO4/C Composite Cathode Material with an Ultrasonic-Intensified Micro-Impinging Jetting Reactor

Electrochemical property of LiFePO4/C composite cathode with different carbon sources

Synthesis of nano FePO 4 and electrochemical characterization of composite cathode material LiFePO 4/C

Synergetic Effect of the Crystallinity, Particle Size of LiFePO4 and the In-Situ Introduced Fe2P on Its High-Rate Capability

Synthesis and electrochemical characterization of LiFePO4/C Cathode materials for Li-ion batteries

Synthesis of LiFePO4/C composite electrode with enhanced electrochemical performance

Preparation and Electrochemical Performance of LiFePO_4/C Using Fe_2O_3 As Raw Material

Electrochemical Performance of LiFe1−xVxPO4/carbon Composites Prepared by Solid-State Reaction

Preparation and properties of LiFePO4/C composite materials with Fe2O3 as starting reactant

Synthesis and Electrochemical Performance of LiFePO4/C Prepared by a New Method

Inorganic-based Sol–gel Synthesis of Nano-Structured LiFePO 4 /C Composite Materials for Lithium Ion Batteries

Synthesis of LiFePO4/C Composite As a Cathode Material for Lithium-Ion Battery by a Novel Two-Step Method

Electrochemical Performance of Nanocrystalline Li3V2(PO4)3/carbon Composite Material Synthesized by a Novel Sol–gel Method

Improved Electrochemical Performances of LiFePO4·Li3V2(PO4)/C Composite Cathode Materials Prepared by Two Simple Solid-State Methods

Synthesis, characterization and properties of LiFePO4/C cathode material

A Novel Synthesis and Characterization of LiFePO4 and LiFePO4/C As a Cathode Material for Lithium-Ion Battery

Synthesis of LiFePO 4 /C Composite Electrode with Enhanced Electrochemical Performance

Li 0.99 Ti 0.01 FePO 4 /C composite as cathode material for lithium ion battery

Electrochemical Performance and Stability of LiMn0.6Fe0.4PO4/C Composite

Li<sub>0.99</sub>Ti<sub>0.01</sub>FePO<sub>4</sub>/C composite as cathode material for lithium ion battery