Abstract:(Fe3-xMnx)(1-delta)O-4 was synthesized using a co-precipitation method and then developed as a catalyst for the low temperature selective catalytic reduction (SCR) of NO with NH3. The SCR activity of (Fe3-xMnx)(1-delta)O-4 was clearly enhanced with the increase of Mn content. The results of in situ DRIFTS study demonstrated that both the Eley-Rideal mechanism (i.e. reaction of activated ammonia with gaseous NO) and the Langmuir-Hinshelwood mechanism (i.e. reaction of adsorbed ammonia species with adsorbed NOx species) might happen during the SCR reaction over (Fe3-xMnx)(1-delta)O-4. According to the kinetic analysis, the respective contribution of the Langmuir-Hinshelwood mechanism and the Eley-Rideal mechanism on the SCR reaction was studied. Only the adsorption of NO + O-2 on (Fe2.8Mn0.2)(1-delta)O-4 was promoted, so the Langmuir-Hinshelwood mechanism predominated over NO conversion on (Fe2.8Mn0.2)(1-delta)O-4 especially at lower temperatures. Both the adsorption of NO + O-2 and the adsorption of NH3 on (Fe2.5Mn0.5)(1-delta)O-4 were obviously promoted, so NO conversion on (Fe2.5Mn0.5)(1-delta)O-4 mainly followed the Eley-Rideal mechanism especially at higher temperatures. Both the nitrate route and the over-oxidization of adsorbed ammonia species contributed to the formation of N2O on (Fe2.8Mn0.2)(1-delta)O-4 above 140 degrees C. However, the formation of N2O on (Fe2.5Mn0.5)(1-delta)O-4 mainly resulted from the over-oxidization of adsorbed ammonia species. Although the activity of (Fe2.5Mn0.5)(1-delta)O-4 was suppressed in the presence of H2O and SO2. the deactivated catalyst can be regenerated after the water washing. (C) 2011 Elsevier B.V. All rights reserved.

Performance of low temperature De-NO_x based on Zr-Mn-Fe/Al_2O_3

Catalytic performance of MnO 2-CeO 2/Ti 0.25Zr 0.25Al 0.5O 1.75 monolith catalyst for low temperature selective catalytic reduction of NO with NH 3

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

De-NOx Study on Alumina Supported Different Metals in Low Temperature

Fe Promotion Effect in Mn-Zr-Fe/Al2O3 for Low -temperature Selective Catalytic Reduction of NO with NH3

Low-temperature selective catalytic reduction of NO with NH3 over MnOx-CeO2/ZrO2-TiO2 monolith catalyst

Low-Temperature Selective Catalytic Reduction of NOx with NH3 over Novel Mn–Zr Mixed Oxide Catalysts

Low-Temperature Selective Catalytic Reduction of NO with NH_3 over MnO_x-CeO_2/ZrO_2-TiO_2 Monolith Catalyst

Low-temperature Selective Catalytic Reduction of NO with NH3 over Monolith Catalyst of MnOx/CeO2–ZrO2–Al2O3

Zr‐doped β‐MnO2 for Low‐temperature Selective Catalytic Reduction of NO by NH3: Preparation, Characterization and Performance

MnOx-Decorated Fe–Zr-Based Nano-Catalysts for Low-Temperature NH3-SCR: Improvement of Catalytic Activity

Fe-Mn/Al2O3 Catalysts for Low Temperature Selective Catalytic Reduction of NO with NH3

Effect of Different Metals for Low Temperature Selective Catalytic Reduction of NO

Preparation and catalytic performance of MnO/TiO2-ZrO2 catalysts used for the selective catalytic reduction of NO at low temperature

Heteroatoms doped iron oxide-based catalyst prepared from zinc slag for efficient selective catalytic reduction of NOx with NH3

Iron, lanthanum and manganese oxides loaded on γ-Al2O 3 for selective catalytic reduction of NO with NH 3 at low temperature

Low-Temperature Selective Catalytic Reduction of NO With NH_3 Over Iron Based Catalysts

Cr–MnO Mixed-Oxide Catalysts for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Low Temperature Selective Catalytic Reduction Of No With Nh3 Over Mn-Fe Spinel: Performance, Mechanism And Kinetic Study

Tunable Highly Dispersed Nia-xMnxAlOy Catalysts Derived from Layered Double Oxide for Low Temperature NOx Removal