Abstract:(Fe3-xMnx)(1-delta)O-4 was synthesized using a co-precipitation method and then developed as a catalyst for the low temperature selective catalytic reduction (SCR) of NO with NH3. The SCR activity of (Fe3-xMnx)(1-delta)O-4 was clearly enhanced with the increase of Mn content. The results of in situ DRIFTS study demonstrated that both the Eley-Rideal mechanism (i.e. reaction of activated ammonia with gaseous NO) and the Langmuir-Hinshelwood mechanism (i.e. reaction of adsorbed ammonia species with adsorbed NOx species) might happen during the SCR reaction over (Fe3-xMnx)(1-delta)O-4. According to the kinetic analysis, the respective contribution of the Langmuir-Hinshelwood mechanism and the Eley-Rideal mechanism on the SCR reaction was studied. Only the adsorption of NO + O-2 on (Fe2.8Mn0.2)(1-delta)O-4 was promoted, so the Langmuir-Hinshelwood mechanism predominated over NO conversion on (Fe2.8Mn0.2)(1-delta)O-4 especially at lower temperatures. Both the adsorption of NO + O-2 and the adsorption of NH3 on (Fe2.5Mn0.5)(1-delta)O-4 were obviously promoted, so NO conversion on (Fe2.5Mn0.5)(1-delta)O-4 mainly followed the Eley-Rideal mechanism especially at higher temperatures. Both the nitrate route and the over-oxidization of adsorbed ammonia species contributed to the formation of N2O on (Fe2.8Mn0.2)(1-delta)O-4 above 140 degrees C. However, the formation of N2O on (Fe2.5Mn0.5)(1-delta)O-4 mainly resulted from the over-oxidization of adsorbed ammonia species. Although the activity of (Fe2.5Mn0.5)(1-delta)O-4 was suppressed in the presence of H2O and SO2. the deactivated catalyst can be regenerated after the water washing. (C) 2011 Elsevier B.V. All rights reserved.

Fe Promotion Effect in Mn-Zr-Fe/Al2O3 for Low -temperature Selective Catalytic Reduction of NO with NH3

Fe Promotion Effect in Mn/Usy for Low-Temperature Selective Catalytic Reduction of No with Nh3

Performance of low temperature De-NO_x based on Zr-Mn-Fe/Al_2O_3

Effect of Different Metals for Low Temperature Selective Catalytic Reduction of NO

Effect of Fe on the Selective Catalytic Reduction of NO by NH3 at Low Temperature over Mn/CeO2-TiO2 Catalyst

Fe-Mn/Al2O3 Catalysts for Low Temperature Selective Catalytic Reduction of NO with NH3

Promoting effect of Cu and Mn doping on the Fe/ZSM-5 catalyst for selective catalytic reduction of NO with NH 3

MnOx-Decorated Fe–Zr-Based Nano-Catalysts for Low-Temperature NH3-SCR: Improvement of Catalytic Activity

Effect of Fe2O3 on ZrTiO4 Support for NH3-SCR Catalytic Performance

Efficient FeMn/Al2O3 catalyst for NH3-SCR of NO at low temperature: the Influence of Strong Interactions Between Active Components and Carrier

Low-Temperature Selective Catalytic Reduction of NOx with NH3 over Fe–Mn Mixed-Oxide Catalysts Containing Fe3Mn3O8 Phase

Influence of the Addition of Transition Metals (cr, Zr, Mo) on the Properties of MnO X –feo X Catalysts for Low-Temperature Selective Catalytic Reduction of NO X by Ammonia

Promotional effect of aluminum doping on the sulfated Fe2O3 catalyst in selective catalytic reduction of NO with NH3

Iron, lanthanum and manganese oxides loaded on γ-Al2O 3 for selective catalytic reduction of NO with NH 3 at low temperature

Enhancement of Low-Temperature Catalytic Activity over a Highly Dispersed Fe–Mn/Ti Catalyst for Selective Catalytic Reduction of NOx with NH3

Efficient Fe-ZSM-5 catalyst with wide active temperature window for NH3 selective catalytic reduction of NO: Synergistic effect of isolated Fe3+ and Fe2O3

Fe–Mn Mixed Oxide Catalysts Synthesized by One-Step Urea-Precipitation Method for the Selective Catalytic Reduction of NOx with NH3 at Low Temperatures

Low Temperature Selective Catalytic Reduction Of No With Nh3 Over Mn-Fe Spinel: Performance, Mechanism And Kinetic Study

Effect of iron loading on the performance and structure of Fe/ZSM-5 catalyst for the selective catalytic reduction of NO with NH3

Comparative study on transition element doped Mn–Zr–Ti-oxides catalysts for the low-temperature selective catalytic reduction of NO with NH3

Effect of Fe2O3/ACF catalysts modified by non-thermal plasma on the selective catalytic reduction of NO at low temperature