Abstract:Fe-ZSM-5 catalysts for selective catalytic reduction (SCR) of NOx with ammonia were prepared by ion exchange under different atmospheres and characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Temperature-programmed desorption of NH3 and NO (NH3-TPD and NO-TPD), Ultraviolet visible (UV-vis) spectroscopy and in situ diffuse reflectance Fourier transform infrared spectroscopy (DRIFT). The results show that the atmosphere during ion exchange and calcination significantly affects the cation exchange capacity and the nature of the Fe species in Fe-ZSM-5 catalysts. An air atmosphere was conducive to improving the ability of ZSM-5 zeolites for Fe ionic exchange. However, isolated Fe3+ sites were dominant in Fe-ZSM-5 catalyst (Fe-Z(N-2)) prepared under a N-2 atmosphere, and small oligomeric FexOy clusters and FexOy nano-particles were markedly increased in Fe-ZSM-5 catalyst prepared in air, resulting in the higher SCR activity and wide temperature window of Fe-Z(N-2). Moreover, Fe-Z(N-2) catalyst possessed more Bronsted acid sites and could adsorb more NH3 species, promoting its SCR activity. In situ DRIFT studies showed that NH3 can be adsorbed on both Bronsted and Lewis acid sites on Fe-ZSM-5 catalyst, and this adsorbed NH3 can react with gaseous NOx. Additionally, NOx can be adsorbed on Fe-ZSM-5 catalyst, mainly as a bidentate nitrate, but these nitrate species cannot be confirmed to react with gaseous NH3 because of the overlap with the strong absorption band of adsorbed NH3 species. Based on the IR results and weak adsorption of NOx over Fe-ZSM-5 catalysts, it was concluded that NH3-SCR over this Fe-ZSM-5 catalyst predominantly follows the Eley-Rideal reaction mechanism. (C) 2016 Elsevier B.V. All rights reserved.

Efficient Fe-ZSM-5 catalyst with wide active temperature window for NH3 selective catalytic reduction of NO: Synergistic effect of isolated Fe3+ and Fe2O3

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Promoting effect of Cu and Mn doping on the Fe/ZSM-5 catalyst for selective catalytic reduction of NO with NH 3

Experimental and Density Functional Theory Studies on the Zeolite-Based Fe–Ni–W Trimetallic Catalyst for High-Temperature NOx Selective Catalytic Reduction: Identification of Active Sites Suppressing Ammonia Over-oxidation

Evolution Mechanism of NOx in NH3-SCR Reaction over Fe-ZSM-5 Catalyst: Species-performance Relationships

Performance of Fe-ZSM-5 for Selective Catalytic Reduction of NO X with NH 3 : Effect of the Atmosphere During the Preparation of Catalysts

Promoting Metal Oxides–zeolite Electron Interaction on MnCeOx/HY Catalyst for Boosting Nitrogen Oxides Reduction

Widened Active Temperature Window of a Fe-ZSM-5 Catalyst by an Impregnation Solvent for NH3-SCR of NO

Mechanistic Study of Selective Catalytic Reduction of NO with NH3 over Highly Dispersed Fe2O3 Loaded on Fe-ZSM-5

Effect of iron loading on the performance and structure of Fe/ZSM-5 catalyst for the selective catalytic reduction of NO with NH3

Effect of Fe2O3 on ZrTiO4 Support for NH3-SCR Catalytic Performance

Catalytic N2O Decomposition and Reduction by NH3 over Fe/Beta and Fe/SSZ-13 Catalysts

N 2 O catalytic reduction by NH 3 over Fe-zeolites: Effective removal and active site

Catalytic Performance of Fe–ZSM-5 Catalysts for Selective Catalytic Reduction of Nitric Oxide by Ammonia

Capability of molecular sieve-supported FeSO_4 catalyst for selective catalytic reduction of NO_x

Optimizing Selective Catalytic Reduction of NO with NH3 on Fe2O3/WO3 Via Redox‐Acid Synergy

Low-temperature Fe–MnO2 Nanotube Catalysts for the Selective Catalytic Reduction of NOx with NH3

Activity enhancement of sulphated Fe<sub>2</sub>O<sub>3</sub> supported on TiO<sub>2</sub> -ZrO<sub>2</sub> for the selective catalytic reduction of NO by NH<sub>3</sub>

Fe-Mn/Al2O3 Catalysts for Low Temperature Selective Catalytic Reduction of NO with NH3

Low-Temperature Selective Catalytic Reduction of NOx with NH3 over Fe–Mn Mixed-Oxide Catalysts Containing Fe3Mn3O8 Phase

Heteroatoms doped iron oxide-based catalyst prepared from zinc slag for efficient selective catalytic reduction of NOx with NH3