Abstract:TiO2-ZrO2 (Ti-Zr) carrier was prepared by a co-precipitation method and 1 wt. % V2O5 and 0.2 CeO2 (the Mole ratio of Ce to Ti-Zr) was impregnated to obtain the V2O5-CeO2/TiO2-ZrO2 catalyst for the selective catalytic reduction of NOx by NH3. The transient activity tests and the in situ DRIFTS (diffuse reflectance infrared Fourier transform spectroscopy) analyses were employed to explore the NH3-SCR (selective catalytic reduction) mechanism systematically, and by designing various conditions of single or mixing feeding gas and pre-treatment ways, a possible pathway of NOx reduction was proposed. It was found that NH3 exhibited a competitive advantage over NO in its adsorption on the catalyst surface, and could form an active intermediate substance of -NH2. More acid sites and intermediate reaction species (-NH2), at lower temperatures, significantly promoted the SCR activity of the V2O5-0.2CeO2/TiO2-ZrO2 catalyst. The presence of O2 could promote the conversion of NO to NO2, while NO2 was easier to reduce. The co-existence of NH3 and O2 resulted in the NH3 adsorption strength being lower, as compared to tests without O2, since O2 could occupy a part of the active site. Due to CeO2’s excellent oxygen storage-release capacity, NH3 adsorption was weakened, in comparison to the 1 wt. % V2O5-0.2CeO2/TiO2-ZrO2 catalyst. If NOx were to be pre-adsorbed in the catalyst, the formation of nitrate and nitro species would be difficult to desorb, which would greatly hinder the SCR reaction. All the findings concluded that NH3-SCR worked mainly through the Eley-Rideal (E-R) mechanism.

Mechanistic Study of Selective Catalytic Reduction of NO with NH3 over Highly Dispersed Fe2O3 Loaded on Fe-ZSM-5

The development of Fe2O3-based catalysts used for the selective catalytic reduction of NOx with NH3: A review

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Selective Catalytic Reduction of NOx with NH3 over Short-Range Ordered W-O-Fe Structures with High Thermal Stability

Selective catalytic reduction of NO over Fe-ZSM-5: mechanistic insights by operando HERFD-XANES and valence-to-core X-ray emission spectroscopy

Kinetics of Selective Catalytic Reduction of NO by NH3 on Fe-Mo/ZSM-5 Catalyst.

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Activation of Fast Selective Catalytic Reduction of NO by NH3 at Low Temperature over TiO2 Modified CuOX-CeOX Composites

Effect of iron loading on the performance and structure of Fe/ZSM-5 catalyst for the selective catalytic reduction of NO with NH3

Catalytic Mechanism Of Nay Zeolite Supported Feso4 Catalyst For Selective Catalytic Reduction Of Nox

A mechanistic investigation of the selective catalytic reduction of NOx with NH3 over supported CeO2/TiO2 catalysts

N 2 selectivity of Fe–Mn nano-sized catalysts in selective catalytic reduction of ammonia

Optimizing Selective Catalytic Reduction of NO with NH3 on Fe2O3/WO3 Via Redox‐Acid Synergy

Insight into highly efficient FeOx catalysts for the selective catalytic reduction of NOx by NH3: Experimental and DFT study

Metal-organic framework assisted preparation of α-Fe2O3 for selective catalytic reduction of NOX with NH3

Promoting effect of Cu and Mn doping on the Fe/ZSM-5 catalyst for selective catalytic reduction of NO with NH 3

Effect of Surface Structure of &Lt;em>&alpha;</em>-Fe<sub>2</sub>o<sub>3</sub> on the Selective Catalytic Reduction of NO by NH<sub>3</sub>

Comparative study of ZSM‐5 supported transition metal (Cu, Mn, Co, and Fe) nanocatalysts in the selective catalytic reduction of NO with NH3

Capability of molecular sieve-supported FeSO_4 catalyst for selective catalytic reduction of NO_x

Selective Catalytic Reduction of NOxwith Ammonia over Fe-Mo/ZSM-5 Catalysts

Catalytic Performance of Fe–ZSM-5 Catalysts for Selective Catalytic Reduction of Nitric Oxide by Ammonia