Abstract:In this study, a new composite of low-temperature selective catalytic reduction (LT-SCR) catalyst is synthesized by impregnating MnOx onto ZnO nanorod arrays integrated with cordierite ceramic substrate (MnOx-ZnO/CC), which exhibits improved activities at 100-250 degrees C compared to its analogue that fabricated from TiO2 nanorod arrays (MnOx-TiO2/CC). By optimizing the synthesis conditions, the MnOx-ZnO/CC catalyst obtains a maximum NOx conversion efficiency of 96.8% at 200 degrees C. The introduction of ZnO nanorod arrays not only provides a high surface area, but also results in the formation of amorphous MnOx. A higher content of Mn4+, proper ratio of surface-adsorbed oxygen (O-alpha), and more Lewis acid sites are found on the surface of the MnOx-ZnO/ CC catalyst than that on the MnOx-TiO2/CC counterpart. Additional information about the reaction mechanism is systematically investigated via in situ diffuse reflectance infrared Fourier transform spectroscopy (in situ DRIFTS), the results of which demonstrate that the LT-SCR reactions over the MnOx-ZnO/CC catalyst generally occur between NOx and NH3 species in the adsorption status, following the Langmuir-Hinshelwood pathway. The enhanced activities can be attributed to the generation of abundant NH4NO3 originating from NO2 in the "Fast SCR" route, because the synergistic effect between MnOx and ZnO facilitates the oxidation of NO.

Low-Temperature Selective Catalytic Reduction of NOx with NH3 over Novel Mn–Zr Mixed Oxide Catalysts

Catalytic performance of MnO 2-CeO 2/Ti 0.25Zr 0.25Al 0.5O 1.75 monolith catalyst for low temperature selective catalytic reduction of NO with NH 3

Low-temperature Selective Catalytic Reduction of NO with NH3 over Monolith Catalyst of MnOx/CeO2–ZrO2–Al2O3

Selective catalytic reduction of NOx with NH3 over Mn–Zr–Ti mixed oxide catalysts

Selective Catalytic Reduction of Nox with Nh3 on A Cr-Mn Mixed Oxide at Low Temperature

Low-temperature selective catalytic reduction of NO with NH3 over MnOx-CeO2/ZrO2-TiO2 monolith catalyst

Manganese–niobium Mixed Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH3 at Low Temperatures

Low-Temperature Selective Catalytic Reduction of NO with NH_3 over MnO_x-CeO_2/ZrO_2-TiO_2 Monolith Catalyst

MnOx-Decorated Fe–Zr-Based Nano-Catalysts for Low-Temperature NH3-SCR: Improvement of Catalytic Activity

Low-Temperature Selective Catalytic Reduction of NOx with NH3 over Fe–Mn Mixed-Oxide Catalysts Containing Fe3Mn3O8 Phase

Cr–MnO Mixed-Oxide Catalysts for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Selective Catalytic Reduction of NO with NH3 on Modified ZrO2-MnO2 Monolithic Catalysts

The activity and characterization of MnOx–CeO2–ZrO2/γ-Al2O3 catalysts for low temperature selective catalytic reduction of NO with NH3

Preparation and catalytic performance of MnO/TiO2-ZrO2 catalysts used for the selective catalytic reduction of NO at low temperature

Preparation of Cr-Mn Mixed Oxide by Coprecipitation and Its Performance for Low-Temperature Selective Catalytic Reduction of NOx

Selective Catalytic Reduction of NOX on Cr-Mn Mixed Oxide at Low Temperature

Selective Catalytic Reduction of NO with NH3 over Mn-based Catalysts at Low Temperature

Manganese Oxide Catalysts Supported on Zinc Oxide Nanorod Arrays: A New Composite for Selective Catalytic Reduction of NOx with NH3 at Low Temperature

Selective Catalytic Reduction of NOx with NH3 over Mn-Ce Mixed Oxide Catalyst at Low Temperatures

Novel Mnox Catalyst for Low-Temperature Selective Catalytic Reduction of Nox with Nh3