Abstract:The effects of Mn loadings and precursors, catalyst preparation methods, incineration durations and temperatures, and the addition of Co and Ce on NO-reduction efficiency and selectivity (N2O formation) during the preparation of MnOx/Ti-based catalysts were studied by micropore-size analysis (XRD, XPS, SEM, and FTIR), while considering changeable parameters. Meanwhile, the performance of low-temperature SCR of NO with NH3 over the designed catalysts was tested under various gas hourly space velocities (GHSVs), NH3/NO molar ratios, and contents of NO, NH3, O-2, H2O, and SO2 in a lab-scale reactor. Overall, the Mn(0.3)Ce(0.1)/Ti catalyst, which had high NO-reduction efficiency and selectivity (low N2O formation), was recommended, with the following preparation methods: ultrasonic impregnation; manganese acetate precursor; and incineration at 500 degrees C. Appropriate textural properties (high surface area and small pore and crystallite sizes), well-dispersed amorphous manganese (rather than crystalline) on the anatase surface (rather than rutile), abundant active sites, and long residence time are essential for high NO-reduction efficiency. In practice, NO-reduction efficiency decreased with increasing GHSV and the NH3 and NO contents; however, it initially increased and then became saturated with an increasing NH3/NO molar ratio and O-2 content. Water deactivated the catalyst to a recoverable state, whereas SO2 resulted in unrecoverable deactivation.

Low-temperature selective catalytic reduction of NO with NH3 over MnOx-CeO2/ZrO2-TiO2 monolith catalyst

Catalytic performance of MnO 2-CeO 2/Ti 0.25Zr 0.25Al 0.5O 1.75 monolith catalyst for low temperature selective catalytic reduction of NO with NH 3

Low-Temperature Selective Catalytic Reduction of NO with NH_3 over MnO_x-CeO_2/ZrO_2-TiO_2 Monolith Catalyst

Low-Temperature Selective Catalytic Reduction of NO with NH3 over MnOx-CeO2/ZrO2-TiO2 Monolith Catalyst

Low-temperature Selective Catalytic Reduction of NO with NH3 over Monolith Catalyst of MnOx/CeO2–ZrO2–Al2O3

Influence of calcination temperature on performance of monolith catalyst MnO2-CeO2/Zr0.25 Ti0.25Al0.5O1.75 for selective catalytic reduction of NO by NH3 at low temperature

Monolith Manganese-Based Catalyst Supported on ZrO2-TiO2 for NH3-SCR Reaction at Low Temperature

Low-Temperature Selective Catalytic Reduction of NOx with NH3 over Novel Mn–Zr Mixed Oxide Catalysts

Influence of Calcination Temperature on Performance of Monolith Catalyst MnO<SUB>2</SUB>-CeO<SUB>2</SUB>/Zr<SUB>0.25</SUB>Ti<SUB>0.25</SUB>Al<SUB>0.5</SUB>O<SUB>1.75</SUB> for Selective Catalytic Reduction of NO by NH<SUB>3</SUB> at Low Temperature

Low-temperature SCR of NO with NH3 over AC/C Supported Manganese-Based Monolithic Catalysts

Selective Catalytic Reduction of NO with NH3 on Modified ZrO2-MnO2 Monolithic Catalysts

Selective catalytic reduction of NOx with NH3 by monolithic catalyst MnOx/AC/C under low temperature in the presence of excess O2

Preparation and catalytic performance of MnO/TiO2-ZrO2 catalysts used for the selective catalytic reduction of NO at low temperature

Preparation of Mn-Fe/ZrO2-TiO2 monolith catalyst and its properties for low-temperature NH3-SCR reaction

Performance of Low-temperature SCR of NO with NH3 over MnOx/Ti-based catalysts

Cr–MnO Mixed-Oxide Catalysts for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Low-Temperature Selective Catalytic Reduction of NO with NH3 Over Mn–Ti Oxide Catalyst: Effect of the Synthesis Conditions

Tungsten Modified MnOx–CeO2/ZrO2 Monolith Catalysts for Selective Catalytic Reduction of NOx with Ammonia

The activity and characterization of MnOx–CeO2–ZrO2/γ-Al2O3 catalysts for low temperature selective catalytic reduction of NO with NH3

Selective Catalytic Reduction of NO with NH3 over Mn-based Catalysts at Low Temperature