Formation and Thermal Properties of B2O3–La2O3–ZnO Glasses for Low Temperature Co-Fired Ceramics

Huixing Lin,Xiangyu Zhao,Wei Chen,Lan Luo

DOI: https://doi.org/10.1016/j.jallcom.2009.01.082

IF: 6.2

2009-01-01

Journal of Alloys and Compounds

Abstract:Glass forming region of B2O3–La2O3–ZnO system was investigated and the influence of ZnO, La2O3 and B2O3 on the transition temperature (Tg) and the coefficient of the thermal expansion of glasses (α) from the ternary system was examined by differential thermal analysis (DTA) and the thermal expansion measurement. This study shows that the effects of B2O3, ZnO and La2O3 are significantly different. Increasing B2O3 content led to the increase of Tg and the decrease of α. When ZnO content was increased, Tg decreased dramatically, but α kept almost unchanged. Tg and α increased when La2O3 content was added. When B2O3–La2O3–ZnO glasses were as sintering aids for low temperature co-fired ceramics, it is important that the thermal properties of the glasses were understood and controlled to meet some compatibility requirement.