Abstract:Arrays of randomly oriented zinc oxide (ZnO) nanowires were fabricated on silicon wafers via a simple thermal evaporation method. During the fabrication, the temperature around the substrate was below 500°C. The products were analyzed by conventional means and determined to be single crystals of wurtzite-type ZnO that grew along the c-axis. These nanowires were 10–100nm in diameter and 10–100μm in length, suggesting a possible high field enhancement factor. The dependence of the field emission current on the anode–cathode voltage (I–V behavior) of the ZnO nanowire arrays was measured in a lab-built ultrahigh vacuum system with a base pressure of 10−7Pa. After surface cleaning by heat treatment, two characteristic electric fields, under which 10μA/cm2 and 1mA/cm2 current densities were extracted, were measured to be 4.0 and 4.7V/μm, respectively. As observed with a transparent anode, emission occurred uniformly over the whole sample surface. A 72h-long test on emission stability was performed under a constant voltage of 2.75kV. The current dropped occasionally to approximately 80% of the initial value during the test owing to the poor adherence of the nanowires to the substrate. These preliminary results have shown the perspective of, as well as a major drawback to, a ZnO nanowire array being developed into a cold electron source to be used in future electronic devices.

Large-scale fabrication of high-purity and uniform Zn nanowires by thermal evaporation

Thermal Evaporation Synthesis of Zinc Oxide Nanowires

Characterization of zinc oxide crystal nanowires grown by thermal evaporation of ZnS powders

Silicon Nano-Wires Fabricated by a Novel Thermal Evaporation of Zinc Sulfide

Growth And Characterization Of Cu-Catalyzed Zno Nanowires

Formation of ZnO nanostructures by a simple way of thermal evaporation

Low-Temperature Growth and Properties of Zno Nanowires

Large-Scale Synthesis of Zno Nanowires Using A Low-Temperature Chemical Route and Their Photoluminescence Properties

On the formation of well-aligned ZnO nanowall networks by catalyst-free thermal evaporation method

Large-Scale Synthesis of Bicrystalline ZnO Nanowire Arrays by Thermal Oxidation of Zinc Film: Growth Mechanism and High-Performance Field Emission

Growth of ultrafine ZnS nanowires

Fabrication and characterization of single-crystalline ZnTe nanowire arrays

Growth and Electrical Properties of Zinc Oxide Nanowires.

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

Field Emission Properties of Zinc Oxide Nanowires Fabricated by Thermal Evaporation

Silicon Nano-Wires Fabricated by Thermal Evaporation of Silicon Wafer

Growth mechanism and diameter control of well-aligned small-diameter ZnO nanowire arrays synthesized by a catalyst-free thermal evaporation method.

Synthesis and Characterization of ZnO Nanowires Using a Simple PVD Approach Without Catalysts

Optical Properties of Zno Nanowires Grown by Thermal Evaporation

Fabrication of ZnO Nanowires by Vapor-Phase Deposition and Their Field Emission Properties

Peculiar Zno Nanopushpins And Nanotubes Synthesized Via Simple Thermal Evaporation